Abstract:The following study focuses on identifying the conditions for codepositing Hf and Al by the pack cementation process to form diffusion coatings on nickel-base superalloys to enhance their high temperature sulfidation/corrosion resistance. Thermochemical calculations were carried out for the pack series Hf–CrCl3·6H2O–Al2O3 with or without elemental Al added. The results obtained were used to identify possible pack compositions suitable for the intended codeposition process by comparing the calculated partial pressures of Hf-, Al- and Cr-chloride vapour species generated at high temperatures. Based on the results of thermochemical calculations, a series of coating deposition experiments were undertaken, which confirmed that codeposition of Al and Hf is possible at 1100 °C in packs of appropriate compositions. It was inferred from the results of both thermochemical calculations and coating deposition experiments that HfCl4 may not be considered as the depositing species for releasing Hf at the substrate surface and that the deposition tendency of these packs can be assessed by comparing the calculated partial pressures of HfCl3, AlCl and CrCl. When the partial pressure of CrCl is far higher than those of HfCl3 and AlCl, the packs have a tendency to deposit only Cr. When the partial pressure of CrCl is lower than that of either HfCl3 or AlCl, and also when the partial pressures of HfCl3 and AlCl is within approximately one order of magnitude, codeposition of Hf and Al may occur within the packs. Under the conditions suitable for codepositing Hf and Al, coatings formed predominantly through the outward Ni diffusion process. The microstructure of coatings depended strongly on the pack composition. It is expected that the deposition parameters, such as pack composition and deposition temperature may be usefully utilised to influence the mechanism and kinetics of the codeposition process and hence to effectively control the microstructure of the coating formed as a result.

Pack codeposition of Al and Cr to form diffusion coatings resistant to high temperature oxidation and corrosion for γ-TiAl

Pack Deposition Of Oxidation Resistant Silicide And Aluminide Coatings On Gamma-Tial

Vapour phase codeposition of Al and Si to form diffusion coatings on γ-TiAl

Codeposition of Al and Si to form oxidation-resistant coatings on γ-TiAl by the pack cementation process

Co-deposition of aluminide and silicide coatings on γ-TiAl by pack cementation process

Pack deposition of coherent aluminide coatings on γ-TiAl for enhancing its high temperature oxidation resistance

Co-Deposition Of Aluminide And Silicide Coatings On Gamma-Tial By Pack Cementation Process

Conditions For Formation Of Coherent Aluminide Coatings On Gamma-Tial By Pack Cementation Process

Conditions for Codeposition of Al and Cr on Ni Base Superalloys by Pack Cementation Process

Conditions for pack codeposition of Al and Hf on nickel-base superalloys

Characterisation and Oxidation Behaviour of Plasma Surface Alloyed on Γ-Tial Alloy

Pack Formation and Long Term Oxidation Kinetics of TiAl3coating Onγ-Tial

Pack Formation And Long Term Oxidation Kinetics Of Tial3 Coating On Gamma-Tial

Pack cementation process for the formation of refractory metal modified aluminide coatings on nickel-base superalloys

Codeposition of Al and Si on nickel base superalloys by pack cementation process

Formation of aluminide coatings on low alloy steels at 650°C by pack cementation process

Pack aluminisation of low alloy steels at temperatures below 700 $deg;C

Aluminide coating formation on nickel-base superalloys by pack cementation process

Pack Aluminide Coatings Formed At 650 Degrees C For Enhancing Oxidation Resistance Of Low Alloy Steels

Deposition of silicon modified aluminide coatings on nickel base superalloys by pack cementation process

Oxidation Resistance of Diffusion Coatings Formed by Pack-Codeposition of Al and Si on Γ-Tial