Microstructure and Electrical Properties of Nb2O5-doping NiFe2O4 Ceramic

王昊,周科朝,李志友
2013-01-01
Abstract:The ceramic powders were synthesized by solid-state reaction method using nickel oxide, ferric oxide and niobium oxide as raw materials, and the Ni1?xNbxFe2O4 (x=0, 0.02, 0.05, 0.07, 0.10 and 0.20) ceramic were prepared by isostatic pressing-atmosphere sintering method. The electronic conductivity of ceramics was tested. The phase composition, microstructure and microarea composition of ceramics were analyzed by XRD, SEM, EDX, FTIR and XPS. The effects of Nb2O5-doping on the microstructure and electrical properties of ceramics were investigated. The results show that the appearance of NiO phase in NiFe2O4 matrix is restrained during Nb2O5-doping. And an impurity phase of FeNbO4 appears while excessive Nb2O5 is added. The right amount of doping (x=0.05) helps to eliminate the pores in grain boundaries and improves the sintering density of ceramics. Compared with the undoped samples, the conductivity performances of doped sample have been greatly improved. The conductivity of Ni0.95Nb0.05Fe2O4 sample increases by 60%compared with that of the undoped samples at 1 233 K.
What problem does this paper attempt to address?