Abstract:In this paper, porous zinc oxide (ZnO) nanosheets were successfully prepared by a simple low-temperature hydrothermal method. X-ray diffraction (XRD), scanning electron microscopy (SEM), transmission electron microscopy (TEM) and Brunauer–Emmett–Teller (BET) tests showed that the synthesized product was ZnO with porous sheet structure. The diameter of porous nanosheets was about 100 nm and the thickness was about 8 nm. As a photocatalyst, the degradation efficiencies of porous ZnO nanosheets for methyl orange (MO), methylene blue (MB) and Rhodamine B (RhB) were 97.5%, 99% and 96.8%, respectively. In addition, the degradation efficiency of ZnO for mixed dyes (Mo, MB and RhB) was satisfactory, reaching 97.7%. The photocatalytic stability of MB was further tested and remained at 99% after 20 cycles. In the experiment, ZnO/FTO (fluorine-doped tin oxide) composites were prepared by using ZnO as the conductive layer. Titanium dioxide (TiO2) was deposited on the surface of ZnO/FTO by electrodeposition, so as to obtain a TiO2/ZnO/FTO composite. By studying the electrochromic properties of this composite, it was found that the TiO2/ZnO/FTO composite shows a large light modulation range (55% at 1000 nm) and excellent cycle stability (96.6% at 200 cycles). The main reason for the excellent electrochromic properties may be the synergistic effect between the porous structure and the polymetallic oxides. This study is helpful to improve the photocatalytic efficiency and cycling stability of metal oxides, improve the transmittance of thin films and provide a new strategy for the preparation of ZnO composite materials with excellent photocatalytic and electrochromic properties.

Synthesis of the Tetrapod-Like ZnO in a Household Microwave Oven

Effect of Solution Concentrations on Crystal Structure, Surface Topographies and Photoluminescence Properties of ZnO Thin Films

Microwave-Assisted Rapid Synthesis Of Zno Hexagonal Quasi-Hourglasses

Zno-based Thin Films Synthesized by Atmospheric Pressure Mist Chemical Vapor Deposition

Rapid synthesis of ZnO micro/nanostructures in large scale

Microwave-assisted synthesis and photocatalytic activity of quantum-sized ZnO

Low-field electron emission from tetrapod-like ZnO nanostructures synthesized by rapid evaporation

A Facile Self-assembly Synthesis of Hexagonal ZnO Nanosheet Films and Their Photoelectrochemical Properties

Enhancement And Patterning Of Ultraviolet Emission In Zno With An Electron Beam

Electrochemical Synthesis for Uniform and Large-Scale Zinc Oxide Nano Structure Films

Controllable Preparation and Photocatalytic Activity of ZnO Microstructures with Different Morphology

Microwave-assisted Preparation, Characterization and Properties of Columnar Hexagonal-Shaped ZnO Microcrystals

Synthesis of ZnO Eggshell-Like Hollow Spheres Via Thermal Evaporation at Low Temperature

Growth Mechanism of ZnO Nanostructures in Wet-Oxidation Process

Synthesis of octahedral ZnO mesoscale superstructures via thermal decomposing octahedral zinc hydroxide precursors

Synthesis and electromagnetic characteristics of ZnO micro-crystal with varying morphology

Self-catalytic Synthesis, Structures, and Properties of High-Quality Tetrapod-Shaped ZnO Nanostructures

Fabrication And Characterization Of Zinc Oxide Films With Ordered Two-Dimensional Pore Arrays

Synthesis of the Porous ZnO Nanosheets and TiO2/ZnO/FTO Composite Films by a Low-Temperature Hydrothermal Method and Their Applications in Photocatalysis and Electrochromism

Controlled Synthesis of Nano-ZnO with Different Morphologies by Hydrolysis in Water Bath/in Microwave with Different Frequency

A Low-Temperature Synthesis of Multiwhisker-Based Zinc Oxide Micron Crystals