Fe-containing mesoporous silicates with macro-lamellar morphology

Yi Lu,Junlin Zheng,Jinku Liu,Jin Mu

DOI: https://doi.org/10.1016/j.micromeso.2007.02.017

IF: 5.876

2007-01-01

Microporous and Mesoporous Materials

Abstract:Fe-containing mesoporous silicates with macro-lamellar morphology were prepared using sodium silicates and Fe(NO3)3 as silica and iron sources in alkaline media, respectively, under the direction of CTAB cationic surfactant. XRD and N2 adsorption results showed that the sample had highly ordered hexagonal mesostructures typical of MCM-41. UV–vis and ESR spectra indicated that most of the iron species were tetrahedrally incorporated into the mesostructured framework in alkaline media. TEM micrographs manifested the macro-lamellar structures when the SiO2/Fe2O3=60 (molar ratio). Additionally, there were many submicron-sized structural defect voids in the mesostructured lamellas. The morphology character underwent huge changes with the increase of Fe(NO3)3 amounts in the synthesis media. When the SiO2/Fe2O3=40, tangled microtubules with about several microns in length dominated the final product. Decreasing the SiO2/Fe2O3 molar ratio to 20, the long cylinders disappeared and 100–600nm sticks represented 80% of the solid material. The dimensions of the resultant sample were reduced with the decrease of SiO2/Fe2O3 molar ratio. The formation mechanism of the macro-lamellar morphology was also proposed on the basis of the previous reports and our characterization results.