Abstract:In this paper, we developed a facile way to synthesize highly ordered optically active MCM-48 at room temperature, by using mixtures of hemicyanine dye N-alkyl-2-[p-(N,N-diethylamino)-o-(alkyloxy)] pyridinium bromide ( denoted as o-CnPOCm, Scheme 1) and cetyltrimethylammonium bromide ( CTAB) as the structure-directing agents. The mesoporous materials were systematically characterized by powder X-ray diffraction, transmission electron microscopy, nitrogen sorption, and thermogravimetry. The resultant MCM-48 exibits unusually high thermal stability. For example, in the case of o-C2POC14, it can retain its cubic structure even under calcinations at 900 degrees C for 5 h, although the pore size is shifted to the micropore region because of shrinkage of the framework. The typical surface area and pore volume are 980 m(2)/g and 0.44 cm(3)/g, respectively, for the powder calcined under such a high temperature. This is the first report of room-temperature synthesis of MCM-48 with such good thermal stability using cationic-cationic mixed surfactant as the structure-directing agent. The fluorescence lifetimes of the as-synthesized mesostructured MCM-48 were also measured, and the result showed that the incorporated dye molecules have a 1 order of magnitude longer lifetime than that of free species in solution, showing that the hemicyanine dye molecules are well dispersed within the CTAB surfactant matrix. Furthermore, we compared eight other dye congeners ( Scheme 1) to fully investigate the mesophase resulting from the dye-CTAB system. The results show that, upon addition of the dye surfactant to the starting mixtures, the mesostructured silica undergoes an intrinsic phase-transition process; however, specific dye geometry is required to obtain MCM-48 at room temperature. Those functionalities as well as the designed synthesis of this novel mesostructured MCM-48 material promise a bright future in multifunctional optical and electric nano- and microdevices (e.g., waveguides, laser, light-emitting diodes, etc.) and also shed light on the self-assembly behavior in complex colloidal system.

Synthesis of bilayer SDS/ionic liquid stabilized ferrofluid and magnetic cubic mesoporous silica by long chain ionic liquid

Fabrication of silica nanoparticles with both efficient fluorescence and strong magnetization, and exploration of their biological applications

Tuning Surface, Phase, and Magnetization of Superparamagnetic Magnetite by Ionic Liquids: Single-Step Microwave-Assisted Synthesis.

Preparation and Characterization of Polydimethylsiloxane Based Magnetic Fluid

Preparation and Characterization of High Stability Silicone-Based Colloidal Magnetic Fluids

An Interface Coassembly in Biliquid Phase: Toward Core-Shell Magnetic Mesoporous Silica Microspheres with Tunable Pore Size

Synthesis of silica-coated polygonal Fe3O4 nanoparticles

Synthesis, Surface Modification and Characterization of Magnetic Fe3O4@SiO2 Core-Shell Nanoparticles

Monodisperse core-shell structured magnetic mesoporous aluminosilicate nanospheres with large dendritic mesochannels

Synthesis of Ferrite Nanocrystals Stabilized by Ionic-Liquid Molecules Through A Thermal Decomposition Route

Imidazolium based Ionic liquid Anchored over Dendritic Mesoporous Silica Nanospheres possessing a Magnetic Core as an Efficient and Recyclable Base Catalyst

Synthesis of Core–Shell Magnetic Nanoparticles Containing Ultrasmall Domains of Silicalite‐1

Hemicyanine dye as a surfactant for the synthesis of bicontinuous cubic mesostructured silica.

Magnetic Fe 3O 4mesoporous silica composites for drug delivery and bioadsorption

Facile Preparation of Superparamagnetic Fe3O4/poly(St-co-MPS)/SiO2 Composite Particles with High Magnetization by Introduction of Silanol Groups.

Synthesis of Fe2SiO4-Fe7Co3 Nanocomposite Dispersed in the Mesoporous SBA-15: Application as Magnetically Separable Adsorbent

Preparation and performance studies of Fe3O4@SiO2 silicon oil based magnetic fluid

Ionic liquid-modulated synthesis of ferrimagnetic Fe3S4 hierarchical superstructures

Surface Organic Modification of Magnetic Iron Oxide Black Particles

Preparation and Characterization of Silicon Oil Based Ferrofluid

Preparation and characterization of water-soluble monodisperse magnetic iron oxide nanoparticles via surface double-exchange with DMSA