Abstract:In this article, we report a controllable and reproducible approach to prepare highly ordered 2-D hexagonal mesoporous crystalline TiO2-SiO2 nanocomposites with variable Ti/Si ratios (0 to infinity). XRD, TEM, and N2 sorption techniques have been used to systematically investigate the pore wall structure, and thermal stability functioned with the synthetic conditions. The resultant materials are ultra highly stable (over 900 degrees C), have large uniform pore diameters (approximately 6.8 nm), and have high Brunauer-Emmett-Teller specific surface areas (approximately 290 m2/g). These mesostructured TiO2-SiO2 composites were obtained using titanium isopropoxide (TIPO) and tetraethyl orthosilicate (TEOS) as precursors and triblock copolymer P123 as a template based on the solvent evaporation-induced co-self-assembly process under a large amount of HCl. Our strategy was the synchronous assembly of titanate and silicate oligomers with triblock copolymer P123 by finely tuning the relative humidity of the surrounding atmosphere and evaporation temperature according to the Ti/Si ratio. We added a large amount of acidity to lower condensation and polymerization rates of TIPO and accelerate the rates for TEOS molecules. TEM and XRD measurements clearly show that the titania is made of highly crystalline anatase nanoparticles, which are uniformly embedded in the pore walls to form the "bricked-mortar" frameworks. The amorphous silica acts as a glue linking the TiO2 nanocrystals and improves the thermal stability. As the silica contents increase, the thermal stability of the resulting mesoporous TiO2-SiO2 nanocomposites increases and the size of anatase nanocrystals decreases. Our results show that the unique composite frameworks make the mesostructures overwhelmingly stable; even with high Ti/Si ratios (> or =80/20) the stability of the composites is higher than 900 degrees C. The mesoporous TiO2-SiO2 nanocomposites exhibit excellent photocatalytic activities (which are higher than that for commercial catalyst P25) for the degradation of rhodamine B in aqueous suspension. The excellent photocatalytic activities are ascribed to the bifunctional effect of highly crystallized anatase nanoparticles and high porosity.

Preparation of Porous TiO2/silica Composites Without Any Surfactants

PREPARATION OF NANO TiO2 ON SURFACE OF SILICA

Preparation of TiO2/SiO2 Composite by Chemical Coating Method

A High-Stability Silica–clay Composite: Synthesis, Characterization and Combination with TiO2 As a Novel Photocatalyst for Azo Dye

Preparation and Properties of TiO2/illite Composites Synthesized at Different Hydrothermal Ph Values

Interface Actions Between TiO2 and Porous Diatomite on the Structure and Photocatalytic Activity of TiO2-diatomite

Controllable and Repeatable Synthesis of Thermally Stable Anatase Nanocrystal-Silica Composites with Highly Ordered Hexagonal Mesostructures.

Chronic constipation in overweight children.

Synthesis and characterization of Ti-SBA-16 ordered mesoporous silica composite

Fabrication of porous silver/titania composite hollow spheres with enhanced photocatalytic performance

Effect of Embedded-Silica on Microstructure and Photocatalytic Activity of Titania Prepared by Ultrasound-Assisted Hydrolysis

Highly Photocatalytic TiO 2 Interconnected Porous Powder Fabricated by Sponge-Templated Atomic Layer Deposition

Three-dimensional Interconnected Mesoporous Anatase TiO2 Exhibiting Unique Photocatalytic Performances

Novel Tio2-Pt@Sio2 Nanocomposites With High Photocatalytic Activity

Preparation and Characterization of Hierarchically Porous Monolithic TiO2

Novel TiO₂-Pt@SiO₂ nanocomposites with high photocatalytic activity

Facile Synthesis of SiO 2 @tio 2 Hybrid NPs with Improved Photocatalytic Performance

Obtaining and Properties of a Photocatalytic Composite Material of the “SiO2–TiO2” System Based on Various Types of Silica Raw Materials

Simple preparation of sub-micron mesoporous TiO2 spheres consisting of anatase nanocrystals

Preparation of porous rutile titania from ilmenite by mechanical activation and subsequent sulfuric acid leaching

Facile synthesis of mesoporous titanium dioxide nanocomposites with controllable phase compositions by microwave-assisted esterification