Structure and Properties of Chitin/alginate Blend Membranes from NaOH/urea Aqueous Solution.
Guoxiang Li,Wangzhou Li,Hongbing Deng,Yumin Du
DOI: https://doi.org/10.1016/j.ijbiomac.2012.08.030
IF: 8.2
2012-01-01
International Journal of Biological Macromolecules
Abstract:Chitin/alginate (CA) blend membranes were successfully prepared from 8wt% NaOH/4wt% urea aqueous solution by coagulating with 0.5M CaCl2 aqueous solution containing 5wt% HCl. Morphology, mechanical properties, thermal stability, and antimicrobial effects of the membranes were investigated by scanning electron microscopy, IR and UV spectroscopes, X-ray diffraction, tensile tests, thermogravimetric analysis, water swelling and antimicrobial tests. The CA blends were miscible when the content of alginate was range from 33 to 67wt%. The crystallinity of the blend membranes decreased with an increase of alginate. Comparing with chitin membranes, the tensile strength and breaking elongation of the blend membranes were obviously improved in dry and wet states. The best values of the tensile strength and breaking elongation were 48MPa and 27%, respectively. All the blend membranes still retained obvious antimicrobial effects toward S. aureus and E. coli. Therefore, they showed potential for biomedical application.