Rheological Study on O−carboxymethylated Chitosan/cellulose Polyblends from LiCl/N,N‐dimethylacetamide Solution

Z Li,XP Zhuang,XF Liu,YL Guan,KD Yao
DOI: https://doi.org/10.1002/app.11790
IF: 3
2003-01-01
Journal of Applied Polymer Science
Abstract:An O-carboxymethylated chitosan (O-CMCh) water solution (I) and NN-dimethylacetamide (DMAc) emulsion (II) were blended with a cellulose LiCl/DMAc solution, and corresponding polyblends (Polyblends I and II) were obtained. The rheology of the three fluids, that is, the cellulose solution and Polyblends I and II, was investigated. The cellulose solution was characterized by a power-law fluid. When an O-CMCh water solution or DMAc emulsion was added to the cellulose solution, the power-law curve was preserved. The power-law indexes (n) of all three fluids increased along with the temperature. Polyblend I displays an n close to but a little higher than that of the cellulose solution, while Polyblend II shows a much higher power index than those of the other two fluids. The values of the apparent viscosity (eta(a)) for all the three fluids are close and decrease along with an increase in the temperature. Adding O-CMCh microparticles into Polyblends I and II results in a decrease in the structural viscosity index (Deltaeta) in comparison to that of the cellulose solution, and this effect is very obvious for Polyblend I. A cellulose solution's Deltaeta declines with the augmentation of temperature, while the Deltaeta's of both Polyblends I and II show minimum values at about 323 K. (C) 2003 Wiley Periodicals, Inc.
What problem does this paper attempt to address?