Effect of Pre-Annealing on Microstructures and Soft Magnetic Properties of Nanocrystalline Fe86Zr7B6Cu1 Alloy

TANG Jian-cheng,WU Ai-hua,ZHANG Meng,LIU Wen-sheng

DOI: https://doi.org/10.3321/j.issn:1004-0609.2007.10.006

2007-01-01

Abstract:The effect of pre-annealing at higher temperature for short duration before conventional annealing at 600 ℃ for 1 h on the crystallization process of amorphous Fe86Zr7B6Cu1 alloy was studied.The affecting mechanism of pre-annealing on the crystallization process of amorphous Fe86Zr7B6Cu1 alloy is discussed by analyzing the temperature dependence of the nucleation rate and the grain growth rate.It is shown that proper pre-annealing leads to the decrease of the grain size and the increase of the volume fraction of crystalline α-Fe in nanocrystalline Fe86Zr7B6Cu1 alloy.BCC α-Fe with grain size of 9.5 nm and volume fraction of 72.4% is formed in ribbon after it has been pre-annealed at 750 ℃ for 2 min followed by conventional annealing at 600 ℃ for 1 h.The grain size and volume fraction of crystalline α-Fe in ribbon annealed at 600 ℃ for 1 h are 13.2 nm and 65.2%,respectively.Complex permeability spectra show that pre-annealing at 750 ℃ for 2 min before conventional annealing at 600 ℃ for 1 h results in a distinct improvement of soft magnetic properties.