Comparative study of the reactive elements effects on oxidation behavior of a Ni-based superalloy
Khalil Rehman,Naicheng Sheng,Zhiru Sang,Shuling Xun,Zhenjiang Wang,Jun Xie,Guichen Hou,Yizhou Zhou,Xiaofeng Sun
DOI: https://doi.org/10.1016/j.vacuum.2021.110382
IF: 4
2021-09-01
Vacuum
Abstract:<p>Hf, Y, and Ce (0.1 wt % each) were added in Ni-based superalloy, prepared by vacuum induction melting (VIM), and their effects on oxidation behavior were investigated after 300 h, over the temperature range 900–1100 °C. The surface of the oxide layer predominantly consisted of Al<sub>2</sub>O<sub>3</sub> and NiO at 900 <sup>°</sup>C. At 1000 <sup>°</sup>C, most of the surface is covered by Al<sub>2</sub>O<sub>3</sub> along with a small amount of NiAl<sub>2</sub>O<sub>4</sub>. However, at 1100 <sup>°</sup>C, the oxide layer's surface mainly formed of NiAl<sub>2</sub>O<sub>4</sub> with plate-like α-Al<sub>2</sub>O<sub>3</sub>. It has been found that Hf produced excellent oxidation resistance and improved the scale adhesion to the alloy surface. On the other hand, Ce has a limited effect at high temperatures, and the scale adhesion is decreased with increasing oxidation time. From the analysis of oxidation kinetics and microstructure, it has been proposed that the dynamic segregation of reactive elements does not physically leads to the blocking of ions outward diffusion through Al<sub>2</sub>O<sub>3</sub>. The improvement in oxidation resistance of alumina forming alloys produced by reactive elements is explained based on ionic radii, chemical reactivity with alloying elements, and alteration in the alumina grain boundary's electronic properties.</p>
materials science, multidisciplinary,physics, applied