Effect of the Calcination Temperature on the Magnetic and Transport Properties of Rhombohedral LaMnO3+δ Compounds

X. L. Wang,D. Li,C. X. Shi,B. Li,T. Y. Cui,Z. D. Zhang

DOI: https://doi.org/10.1016/j.physb.2009.12.001

2010-01-01

Abstract:Rhombohedral LaMnO3+δ powders were successfully synthesized by annealing gel precursors obtained by a polymerized complex method. The average grain size increases with increasing calcination temperature. The zero-field-cooled (ZFC) and field-cooled (FC) magnetization curves indicate that LaMnO3+δ compounds obtained at 700 and 800°C are ferromagnetic, while both ferromagnetic and antiferromagnetic components are present in those calcined at 900 and 1000°C. This is because the concentration of Mn4+ ions drops with increasing calcination temperature. The temperature dependence of the resistivity of LaMnO3+δ compounds exhibits an insulator–metal transition at about 90K and also a low-temperature upturn with a resistivity minimum at about 40K. Upon increasing particle size, the zero-field resistivity of the LaMnO3+δ powders increases due to suppression of the conduction by the insulating antiferromagnetic component. The negative magnetoresistance of a sample pellet prepared at 700°C ranges from −82% to −88% in the temperature range of 40–100K due to suppression of the spin-dependent scattering by an applied field.