Abstract:SiBONC ceramic powders with specific structural characteristics and free boron oxide were designed at atom level, The preparation of polymer precursors synthesized by chloro-polysiloxane, alkyl-amine and boron trichloride to ceramic composite can provide control of the resulting microstructure as well as the desired uniform distribution of phase. Organo-polymeric precursors prepared by polymer precursor method are used to produce ceramic nano-powders through pyrolysis. The ratio of the Si:B is 80:20. The nano-powders was anneal through the hot-pressing method to form the composite ceramics. The features and morphologies of the produced ceramics were investigated by means of mechanics analysis, XRD, FT-IR, SEM and TEM techniques. Experimental results: the density of SiBONC ceramics is between 1.95 g/cm(3) and 2.15 g/cm(3), the flex strength maximizing 150.50 MPa, the Vickers-hardness is 3.78 GPa, the fracture toughness is 2.10 MPa.m(1/2). SiBONC ceramics tan keep the amorphous state at 1700 degrees C, even at 1800 degrees C, the a-SiC can be crystallized from the matrix, the mean grain size is about 100 nm, which indicates that adulterates B, C, N at atom level can obvious increase the crystallize temperature and mechanical property of SiBONC ceramics. Therefore the thermal stability of SiBONC ceramics can, be extraordinary increased.

Preceramic polymer for SiBNC fiber via one-step condensation of silane, BCl<sub>3</sub>, and silazane

Preparation and Characterization of Polymer-Derived Si-B-N-C Fibers

Synthesis of novel SiBNC fiber precursor by a one-pot route

Fine-diameter Si–B–C–N ceramic fibers enabled by polyborosilazanes with N–methyl pendant group

Preparation of high performance Si-B-N ceramic fibers by polymer derived method

Synthesis and characterization of polyborosilazane as novel precursor to SiBNC ceramic

Synthesis and Characterization of Silicon-containing Polyborazine to Boron Nitride Ceramic Fiber

Preparation Of Sibnc Ceramics By Polymer Pyrolysis

Polymer-Ceramic Conversion of Liquid Polyborosilazanes

Preparation of Hollow Si-B-N Ceramic Fibers by Partial Curing and Pyrolysis of Polyborosilazane Fibers

A Novel Polyborosilazane for High-Temperature Amorphous Si–B–N–C Ceramic Fibres

Preparation of Boron Nitride Ceramic Fibers by Pyrolysis of Silicon-containing Polyborazine

A Simple and Efficient Method for the Synthesis of SiBNC Ceramics with Different Si/B Atomic Ratios

Preparation And Characterization Of Polymer-Derived Sibonc Bulk Ceramics By Polymer-Drived Precursor Method

Preceramic Polymer As Precursor for Near‐stoichiometric Silicon Carbon with High Ceramic Yield

Amorphous Fine-Diameter SiC-based Fiber from a Boron-Modified Polytitanocarbosilane Precursor

Soluble and meltable hyperbranched polyborosilazanes toward high-temperature stable SiBCN ceramics.

Chemical Composition and Porous Structure of Polymer‐derived Silicoboron Carbonitride Ceramics Prepared Via a Monomer Route

SYNTHESIS AND CHARACTERIZATION OF POLYNIOBIUMCARBOSILANE TO SiC(Nb)CERAMIC FIBERS

Polyborosilazanes with Controllable B/N Ratio for Si–B–C–N Ceramics

Preparation and properties of SiC nanocrystallite reinforced amorphous Si-B-C-N ceramics