Abstract:TiO2/SBA-15 catalysts, TiO2 nanoparticles well dispersed on SBA-15 supporter, have been successfully obtained through a self-assembly aging, carboxylation and subsequent solvothermal process. Firstly, P123 (PEG-PPG-PEG), KCl, (2-cyanoethyl) triethoxysilane (CETES) and tetraethoxysilane (TEOS) were employed to form cyano-modified SBA-15 (CN/SBA-15) in 2.0 mol/L HCl solution by Self-assembly aging method. Secondly, carboxyl-modified SBA-15 (COOH/SBA-15) was got through carboxylation treatment in 48% H2SO4 solution at 95 degrees C for 24 h. Finally, highly dispersed TiO2/SBA-15 catalysts were successfully synthesized via solvothermal method at 220 degrees C for 12 h using COOH/SBA-15 and tetrabutyl titanate (TB) as raw materials. In order to remove the organic compounds and improve the crystallization of TiO2, the obtained TiO2/SBA-15 catalysts then were filtrated, washed by absolute ethanol for three times, dried at 80 degrees C and calcined at 550 degrees C for 4 h. Notably, the self-assembly and carboxylation process produced large number of good dispersive carboxyl groups (COOH) on SBA-15, which could effectively anchored TB molecules on SBA-15 to promise the highly dispersion of TiO2 on SBA-15. The obtained TiO2/SBA-15 catalysts have been characterized by X-ray diffraction (XRD), Raman spectrum, Fourier transform infrared spectroscopy (FT-IR), transmission electron microscopy (TEM), nitrogen adsorption and UV-Visible diffuse reflectance spectroscopy (UV-Vis). Above results indicate that the TiO2/SBA-15 catalysts exhibit large specific surface area and TiO2 on SBA-15 supporter is anatase phase, they are both play important roles in photocatalytic application. In the current manuscript, the photocatalytic reduction of CO2 under UV light irradiation as a prober reaction was used to investigate the photocatalytic performance of TiO2/SBA-15 catalysts. It was found that the obtained catalysts performed high photocatalytic capacity for CO2 reduction, especially when the loading amount of TiO2 was around 16.5 wt% [n(COOH)/n(TB)=3], the methanol production got maximum which could reach 80 mu mol/g-catalyst after 6 h UV light irradiation. Compared with the catalysts which synthesized through simple impregnation method, our TiO2/SBA-15 catalysts showed the higher activity in photocatalytic reduction of CO2, owing to the better dispersion and crystallization.

Study of Photocatalytic Reduction of CO_2 with H_2O Vapor on CuO_x/TiO_2

Enhanced Photothermal Catalysis for CO2 Reduction with H2O by Amphoteric Metal Oxides Modified TiO2

Photocatalytic CO2 reduction with water vapor to CO and CH4 in a recirculation reactor by Ag-Cu2O/TiO2 Z-scheme heterostructures

Photocatalytic Reduction of CO2 with H2O on Pt-loaded TiO2 Catalyst

Efficient CO2 Reduction with H2O Via Photothermal Chemical Reaction Based on Au-MgO Dual Catalytic Site on TiO2

Dioxygen-enhanced CO2 photoreduction on TiO2 supported Cu single-atom sites

Photothermal Catalysis for Selective CO2 Reduction on the Modified Anatase TiO2 (101) Surface

Copper‐Decorated Microsized Nanoporous Titanium Dioxide Photocatalysts for Carbon Dioxide Reduction by Water

Synthesis of Supported TiO2/SBA-15 Catalysts and Their Performance on Photocatalytic Reduction of CO2

High Efficient Photoreduction CO2 with H2O on Metal Cu-Modified Graphitic Ordered Mesoporous Carbon Supported TiO2 Catalysts under Simulated Solar

Designed synthesis of Cu2O quantum dots/TiO2 nanotubes heterostructure as a photocatalyst for converting CO2 to CH4

Exploring the CO2 reduction reaction mechanism on Pt/TiO2 with the ambient-pressure X-ray photoelectron spectroscopy

Catalytic oxidation of CO over CuO@TiO2 catalyst: The relationship between activity and adsorption performance

Achieving simultaneous Cu particles anchoring in meso-porous TiO2 nanofabrication for enhancing photo-catalytic CO2 reduction through rapid charge separation

Effect of Pretreatment Atmosphere on CuO/TiO2 Activities in NO + CO Reaction

Enhanced Photocatalytic Performance Toward CO2 Hydrogenation over Nanosized TiO2-Loaded Pd under UV Irradiation

Interface engineering of Platinum-Copper alloy/titanium dioxide for enhanced photocatalytic carbon dioxide reduction

Effective CH4 production from CO2 photoreduction using TiO2/xmol% Cu–TiO2 double-layered films

Photothermocatalytic Removal of CO and Formaldehyde with Excellent Water Vapor Stability over Dual‐Functional Copper Loading on TiO 2 Synthesized via Flame Spray Pyrolysis

Hollow cubic TiO2 loaded with copper and gold nanoparticles for photocatalytic CO2 reduction

Oxygen Vacancy Enhanced Photocatalytic Activity of Cu2O/TiO2 Heterojunction