The adsorption performance of high crystallinity Na-p zeolites prepared from oil shale ash for the waste water treatment
Xuejian Zhang,Rui Wang,Fanping Meng,Yongtao Li,Jie Chen,Yusheng Gao,Jinyi Zhang,Weidong Ai,Kuishan Wang,Chenyang Zhang,C.K Mahadevan
DOI: https://doi.org/10.1080/15567036.2024.2417035
2024-10-26
Energy Sources Part A Recovery Utilization and Environmental Effects
Abstract:The Na-p type zeolite has been prepared by the alkali fusion hydrothermal synthesis method using the pure oil shale ash (OSA) and mixture of OSA and coal fly ash (CFA) as raw materials, which was used for adsorption of methylene blue (MB). The XRD spectra of zeolite synthesized from pure oil shale residue under different conditions indicated that the optimal experimental conditions were determined as follows: acid leaching concentration of 10%, sodium hydroxide dosage of 7 g, crystallization temperature of 130°C, and crystallization time of 12 h. Under the same conditions, zeolite was synthesized using the mixture of OSA and CFA, and its properties were characterized using XRD, SEM, and BET techniques. The results showed that the specific surface area and crystallinity of the zeolite prepared from the mixture were 59.6 m 2 /g and 86.32%, respectively, which were higher than that of pure OSA (20.6 m 2 /g and 64.07%). When 0.05 g of zeolite was added to the 35 mg/L MB solution and adsorbed for 180 min, the removal rates of MB by pure OSA, single-source zeolite and zeolite prepared from the mixture were 27.6%, 83.4%, and 99.2%, respectively. The adjusted R square verified that the pseudo-second-order kinetics and Langmuir isotherm model were the best fitting models. The maximum adsorption capacity (Q max ) of zeolite prepared from the mixture for MB was 55.5 mg/g. The above results proved that the novel material prepared in this study could be a potential effective wastewater treatment material.
energy & fuels,engineering, chemical