Abstract:Carbon deposition from catalytic methane decomposition has drawn increasing interest recently. Previously, we have found the carbon formation depends on the crystalline structure of the support, following the trend of Ni/CeO2 > Ni/CaO > Ni/MgO, because Ni supported on MgO is uniformly dispersed and can stabilize high-x CHx intermediates. We have also found that the addition of Pt can inhibit the carbon deposition on Co/Al2O3, because the alloying between Pt and Co results in the better dispersion of Co on the support. Furthermore, it was revealed that by judging the Ni/Mg molar ratio from 1 to 0.25 we could reduce the diameter of deposited carbon nanotubes from 20 to 12 nm, with substantially smaller production rate. All of these previous studies indicated that better dispersion of the supported metal would benefit the decreasing of carbon deposition. Here we present our recent investigation of the effect of support particle size on the carbon deposition. Three different types of 10 wt% Co/Al2O3 catalysts were prepared: Co on commercial Al2O3 (Cat 1), Co on sol-gel-processed Al2O3 (Cat 2), and sol-gel-made homogeneous Co-in-Al2O3 (Cat 3). TEM showed that the diameter of the Co3O4 particles in sol-gel Al2O3, is only around 6 nm, while it is 20-40 nm in the commercial catalyst. By using XRD and FTIR, Co was identified as crystalline Co3O4, in the as-prepared Cat 1 sample, CoAl2O4 in Cat 2, and amorphous Al2O3, in Cat 3, indicating the best dispersion in Cat 3. Methane CO2 reforming was studied on the three catalysts. Longer lifetime was measured for Cat 3 as compared to those on Cat 1 and Cat 2 (>20 h vs. 1 h). The support size effect is discussed.

Carbon Nanotubes Via Methane Decomposition on an Alumina Supported Cobalt Aerogel Catalyst

Methane Catalytic Cracking to Make Hydrogen and Graphitic Nano Carbons (nanotubes, Microfibers, Microballs, Onions) with Zero Emission

Preparation of Nanosized Iron Catalyst and Small Diameter Carbon Nanotubes from Methane Decomposition

Thermo-catalytic methane decomposition over unsupported Fe–Al and Co–Al catalysts for hydrogen and carbon nanostructures production

Effect of Nanostructured Supports on Catalytic Methane Decomposition

Catalytic methane decomposition on CNT-supported Fe-catalysts

Catalytic Chemical Vapor Deposition of Methane to Carbon Nanotubes: Copper Promoted Effect of Ni/MgO Catalysts

In Situ Carbon Nanotube Synthesis by the Reduction of NiO/γ-Al2O3 Catalyst in Methane

Formation of carbon nanofibers/nanotubes by chemical vapor deposition using Al2O3/KOH

Cobalt Supported Nickel Silicate Nanotubes for Efficient CO2 Methanation

Carbon nanotubes containing iron and molybdenum particles as a catalyst for methane decomposition

Synthesis of Thin-Walled Carbon Nanotubes from Methane by Changing the Ni/Mo Ratio in a Ni/Mo/MgO Catalyst

Cobalt promoted Ni/MgAl2O4 catalyst in lean methane catalytic oxidation

Reinforcing hydrogen and carbon nanotube co-production via Cr–O–Ni catalyzed methane decomposition

Synthesis Of Carbon Nanotubes By Catalytic Decomposition Of Methane Using Lani5 Hydrogen Storage Alloy As A Catalyst

Co-Ni on zirconia and titania catalysts for methane decomposition to hydrogen and carbon nanomaterials: The role of metal-support interactions

Enhanced Activation and Decomposition of CH4 by the Addition of C2H4 or C2H2 for Hydrogen and Carbon Nanotube Production

PREPARATION OF HYDROGEN AND CARBON NANOTUBES via METHANE DECOMPOSITION IN FLUIDIZED-BED REACTOR

Application of Carbon Nanotube Supported Nickel/aluminum Mixed Oxide in the Synthesis of Carbon Nanotubes

Nanocatalysts Anchored on Nanofiber Support for High Syngas Production Via Methane Partial Oxidation

Enhanced Production of Carbon Nanotubes: Combination of Catalyst Reduction and Methane Decomposition