Abstract:As a pathway to green hydrogen, the catalytic dehydrogenation of methane is an economical and CO x -free alternative to produce sufficient volumes of hydrogen to address energy sustainability. This work attempts to develop a catalyst to enhance conversion, stability, and favorable carbon nanostructures. Monometallic Fe catalysts were synthesized on a mesoporous carbon template to identify the best catalyst synthesis methodology covering incipient wetness, hydrothermal, and wet impregnation methods. As a logical step to enhance the conversion, stability, and ease of separation of the catalyst from the product carbon, a bimetallic Fe–Mo was synthesized on the same mesoporous carbon template for the first time, using the hydrothermal method, by varying the Mo loading from 2.5 to 15%. The optimal catalyst design had a composition of 30%Fe–5%Mo with a specific surface area of 606.9 g/m2, offering the highest conversion and stability, at a temperature of 950 °C. The highest conversion corresponded to the lowest space velocity, highest reaction temperature, and highest CH4 concentration, with a maximum conversion of 90% and being stable until the end of 2 h of reaction time. X-ray diffraction analysis revealed the presence of Fe2O3 and mixed oxides, Fe2(MoO4)3 and FeMoO4 in the bimetallic catalyst. The initial H2 yield was ∼61%, and it decreased during the reaction, reaching 48% after 4 h of reaction. Various structural, textural, and morphological characterizations of the catalyst pre- and postreaction were performed using advanced analytical techniques. Graphitic carbon, an Fe–Mo alloy, and FeMoO4 phases were observed by XRD patterns of the spent catalyst. Carbon depositions with varying morphologies were observed under different reaction conditions ranging from carbon nanoparticles and carbon nanotubes to agglomerates of nanoparticles and nanoflowers. A well-defined network of carbon nanoflowers along with bamboo-shaped carbon nanotubes could be observed over the surface of the best catalyst under the optimized reaction conditions.

Carbon nanotubes containing iron and molybdenum particles as a catalyst for methane decomposition

Methane Catalytic Cracking to Make Hydrogen and Graphitic Nano Carbons (nanotubes, Microfibers, Microballs, Onions) with Zero Emission

Enhanced Activation and Decomposition of CH4 by the Addition of C2H4 or C2H2 for Hydrogen and Carbon Nanotube Production

Methane decomposition to produce hydrogen and carbon nanomaterials over costless, iron-containing catalysts

Catalytic methane decomposition on CNT-supported Fe-catalysts

Preparation of Nanosized Iron Catalyst and Small Diameter Carbon Nanotubes from Methane Decomposition

Reinforcing hydrogen and carbon nanotube co-production via Cr–O–Ni catalyzed methane decomposition

Synthesis of Thin-Walled Carbon Nanotubes from Methane by Changing the Ni/Mo Ratio in a Ni/Mo/MgO Catalyst

Catalytic Decomposition of CH4 to Hydrogen and Carbon Nanotubes Using the Pt(1)-Fe(30)/MCM-41 Catalyst

Implication of iron nitride species to enhance the catalytic activity and stability of carbon nanotubes supported Fe catalysts for carbon-free hydrogen production via low-temperature ammonia decomposition

Synthesis Of Carbon Nanotubes By Catalytic Decomposition Of Methane Using Lani5 Hydrogen Storage Alloy As A Catalyst

Iron promoted MOF-derived carbon encapsulated NiFe alloy nanoparticles core-shell catalyst for CO2 methanation

Simultaneous Production of Hydrogen and Nanocarbon from Decomposition of Methane on a Nickel-Based Catalyst

Catalytic Dehydrogenation of Methane to Hydrogen and Carbon Nanostructures with Fe–Mo Bimetallic Catalysts

Production of Hydrogen and Carbon Nanotubes from Methane Decomposition in A Two-Stage Fluidized Bed Reactor

Lattice Distortion in Co3O4/Mn3O4-Guided Synthesis via Carbon Nanotubes for Efficient Lean Methane Combustion

Mo-Doped Ni/C Catalyst for Improved Simultaneous Production of Hydrogen and Carbon Nanotubes through Ethanol Decomposition

Co-Ni on zirconia and titania catalysts for methane decomposition to hydrogen and carbon nanomaterials: The role of metal-support interactions

PREPARATION OF HYDROGEN AND CARBON NANOTUBES via METHANE DECOMPOSITION IN FLUIDIZED-BED REACTOR

Pt–Co supported on single-walled carbon nanotubes as an anode catalyst for direct methanol fuel cells

Iron Encapsulated Within Pod‐like Carbon Nanotubes for Oxygen Reduction Reaction