Investigation of giant magneto-impedance effect in electroless-deposited CoP/Insulator/BeCu wires

Hai-lin PAN,Jing-ke CHENG,Zhen-jie ZHAO,Jian-zhong RUAN,Xie-long YANG,Wang-zhi YUAN

DOI: https://doi.org/10.3321/j.issn:1001-9731.2007.11.016

2007-01-01

Abstract:By controlling the process conditions the CoP/Insulator/BeCu composite wires with distinct giant magneto-impedance effect(GMI) have been prepared by electroless-deposition on polyester-coated BeCu wires.The as-deposited sample was treated with current annealing.A dramatic increase of the GMI value was observed at a low frequency after current annealing.The maximum GMI ratio reaches about 991% and the field sensitivity amounts to 2.78%/(A·m-1) at 97kHz.The GMI value is above 50% at the frequency range from 3kHz to 30MHz.The properties of magnetization processes for the annealed samples are analyzed via the complex permeability.The real and imaginary part of the complex permeability change significantly with the variation of DC magnetic field after current annealing.