Abstract:Electrospun anatase-phase TiO2 nanofibers with desired morphological structure and relatively high specific surface area are expected to outperform other nanostructures (e.g., powder and film) of TiO2 for various applications (particularly dye-sensitized solar cell and photo-catalysis). In this study, systematic investigations were carried out to prepare and characterize electrospun anatase-phase TiO2 nanofibers with different morphological structures (e.g., solid, hollow/tubular, and porous) and specific surface areas. The TiO2 nanofibers were generally prepared via electrospinning of precursor nanofibers followed by pyrolysis at 500°C. For making hollow/tubular TiO2 nanofibers, the technique of co-axial electrospinning was utilized; while for making porous TiO2 nanofibers, the etching treatment in NaOH aqueous solution was adopted. The results indicated that the hollow/tubular TiO2 nanofibers (with diameters of ∼300–500nm and wall-thickness in the range from tens of nanometers to ∼200nm) had the BET specific surface area of ∼27.3m2/g, which was approximately twice as that of the solid TiO2 nanofibers (∼15.2m2/g) with diameters of ∼200–300nm and lengths of at least tens of microns. Porous TiO2 nanofibers made from the precursor of Al2O3/TiO2 composite nanofibers had the BET specific surface area of ∼106.5m2/g, whereas porous TiO2 nanofibers made from the precursor of ZnO/TiO2 composite nanofibers had the highest BET specific surface area of ∼148.6m2/g.

Synthesis and characterization of rutile-typed TiO2 porous hollow nanofibres via electrospinning

Preparation and Characterisation of Ultrafine and Uniform Tio2 Nanofibres

Preparation and characterization of anatase titanium dioxide fibre by electrospinning

Preparation of Necklace‐Structured TiO2/SnO2 Hybrid Nanofibers and Their Photocatalytic Activity

Electrospun anatase-phase TiO2 nanofibers with different morphological structures and specific surface areas.

Preparation and Photocatalysis of Mesoporous Tio2 Nanofibers Via an Electrospinning Technique

Fabrication and characterization of electrospun titania nanofibers

Fabrication of TiO 2 /sio 2 Hybrid Fibers with Tunable Internal Porous Structures

Structural properties and photoluminescence of TiO2 nanofibers were fabricated by electrospinning

Controllable Fabrication of TiO(2) 1D-Nano/micro Structures: Solid, Hollow, and Tube-in-tube Fibers by Electrospinning and the Photocatalytic Performance.

Synthesis of porous Bi4Ti3O12 nanofibers by electrospinning and their enhanced visible-light-driven photocatalytic properties.

Nanofibers containing TiO2 nanoparticles formed using conventional and non-conventional electrospinning

Synthesis of Titanium Dioxide Nanotubes from Electrospun Fiber Templates

Preparation and Characterization of Electrospun Polyurethane/Inorganic-Particles Nanofibers

Electrospun TiO2–SiO2 Fibres with Hierarchical Pores from Phase Separation

Fabrication of TiO2/WO3 Composite Nanofibers by Electrospinning and Photocatalystic Performance of the Resultant Fabrics

Preparation of Highly Porous Tio2 Nanotubes and Their Catalytic Applications

Fabrication of flexible TiO2 nanofibres by electrospinning and their photocatalytic properties

Preparation and characterization of doped TiO2 nanofibers by coaxial electrospining combined with sol-gel process

Synthesis of mesoporous tungsten oxide nanofibers using the electrospinning method

TiO2–SiO2 composite fibers with tunable interconnected porous hierarchy fabricated by single-spinneret electrospinning toward enhanced photocatalytic activity