Synthesis of mesoporous tungsten oxide nanofibers using the electrospinning method

Tuan-Anh Nguyen,Tae-Sun Jun,Muhammad Rashid,Yong Shin Kim

DOI: https://doi.org/10.1016/j.matlet.2011.05.103

IF: 3

2011-09-01

Materials Letters

Abstract:Mesoporous tungsten oxide nanofibers were synthesized via a 500°C thermal treatment of composite nanofibers prepared by electrospinning an ethanol solution consisting of tungsten ethoxide, P123 triblock copolymer, and polyvinylpyrrolidone. The as-electrospun composites exhibited unwoven nanofibers with an average diameter of 233nm and a smooth surface morphology. During the calcination process, the composite nanofibers were shrunk to 85nm in diameter and converted into rough, wormhole-like nanofibers. These were formed by agglomerating polycrystalline WO3 particles of 10–30nm along the axial direction. Furthermore, a measured pore-size distribution indicated that this nanofiber mat had different types of meso-sized porosities, which may have resulted from their wormhole-like structures and inter-fiber voids. In addition, it was observed to have the intra-grain porosity with the diameter of about 1.0nm.

materials science, multidisciplinary,physics, applied