Abstract:Concrete structures serving in the marine tidal zone usually suffer the most severe degradations due to multiple ions attacks and drying-wetting cycles. This study systematically investigates the influence of multiple ions presented in the seawater on the degradation process of Portland cement mortar under drying-wetting cycles. The interactions between sulfate (SO42-) and magnesium (Mg2+) on the chloride diffusion and damage behaviors of cement mortar were determined. The results show that the SO42- and SO42-+ Mg2+ in composite solution firstly decrease the chloride ingress and then increase the chloride diffusion, while the presence of Mg2+ increases the chloride diffusion of mortar samples regardless of the exposure to the NaCl + MgCl2 or NaCl + MgCl2+Na2SO4 solution, and rich Mg2+ is found at the outer layer. The existence of SO42- and SO42-+ Mg2+ in multiple ions solutions accelerates the degradation progress, whereas the single Mg2+ has negligible effect on the damages of samples. The phase compositions highlight that the Mg2++SO42- in chloride solution increases consumption of portlandite and causes the decalcification of C–S–H, thus aggravating the degradations of mortar. These phase changes are generally agreed with the predictions of a thermodynamic model. Moreover, the microstructure analysis reveals that the presence of Mg2++SO42- coarsens pore structure of matrix and induces a higher porosity, which further accelerates the ingress of corrosive ions.

Precipitating Rate of Ion in Cement-Based Materials

Diffusion Characteristic of Sulfate Anion in Surface Region of Cement Mortar at Early Stage

Chloride Ingress Profiles and Binding Capacity of Mortar in Cyclic Drying-Wetting Salt Fog Environments

Prediction of Effective Chloride Diffusivity of Cement Paste and Mortar from Microstructural Features

Estimation of Ice Formation in Mortar Saturated with Sodium Chloride Solutions

Degradation mechanism of cement mortar exposed to combined sulfate–chloride attack under cyclic wetting–drying condition

EXPERIMENTAL STUDY ON THE CHLORIDE DIFFUSION OF CONCRETE BASED ON ITS PORE STRUCTURE

A New Hydration Kinetic Model Based on Boundary Nucleation and Growth Mechanism with Time-Dependent Growth Rate: Application to Quantitively Characterize the Influence of Alkali on the Early Hydration of Cement

Meso-scale Mechanical Deterioration of Mortar Due to Sodium Chloride Attack

Setting Times of Early-Age Mortars Determined from Evolution Curves of Poisson's Ratio.

Degradation progress of Portland cement mortar under the coupled effects of multiple corrosive ions and drying-wetting cycles

Effect of Mg2+ Ions on the Nucleation Kinetics of Calcium Sulfate in Concentrated Calcium Chloride Solutions

Pore-scale Modeling of Chloride Ion Diffusion in Cement Microstructures

Effect of Metakaolin on the Diffusion Properties of Chloride Ions in Cement Mortar under the Coupling Effect of Multiple Factors in Marine Environment

Analysis of Sulfate Substance Penetration into the Surface Area of Hardened Cement Mortar and Its Reaction Products

Evaluating the chloride diffusion coefficient of cement mortars based on the tortuosity of pore structurally-designed cement pastes

Experiments on Chloride Binding and Its Release by Sulfates in Cementitious Materials

Effects of Different Calcium Sources and Cementation Environments on Microbially Induced Calcium Carbonate Precipitation

Effects of urease and cementing solution concentrations on micro-scale enzymatic mineralization characteristics

Effects of chloride content on early hydration performance of cement pastes

Chloride Binding Capacity and Its Effect on the Microstructure of Mortar Made with Marine Sand