Revealing the effect of minor Ca and Sr additions on microstructure evolution and mechanical properties of Zn-0.6 Mg alloy during multi-pass equal channel angular pressing
He Huang,Huan Liu,Lisha Wang,Kai Yan,Yuhua Li,Jinghua Jiang,Aibin Ma,Feng Xue,Jing Bai
DOI: https://doi.org/10.1016/j.jallcom.2020.155923
IF: 6.2
2020-12-01
Journal of Alloys and Compounds
Abstract:<p>In this study, the microstructure evolution and mechanical properties of Zn-0.6 (wt.%) Mg alloys with minor calcium (Ca) and strontium (Sr) additions (0.1 wt%) during multi-pass equal channel angular pressing (ECAP) were comparatively investigated. The obtained results illustrate that in addition to α-Zn matrix and network-shaped ternary α-Zn + Mg<sub>2</sub>Zn<sub>11</sub> + MgZn<sub>2</sub> eutectic structure, CaZn<sub>13</sub> and SrZn<sub>13</sub> particles are formed in as-cast Zn-Mg-Ca and Zn-Mg-Sr alloys, respectively. The CaZn<sub>13</sub> particles exhibit cuboid shape, and their sizes are much larger than the ellipsoidal SrZn<sub>13</sub> particles. After multi-passes ECAP, both α-Zn grains and eutectic structure are obviously refined owing to the dynamic recrystallization (DRX) process and mechanical crushing effect, while the CaZn<sub>13</sub> and SrZn<sub>13</sub> particles exhibit no obvious change. Moreover, the existence of cuboid CaZn<sub>13</sub> particles with sharp corners are more effective to refine α-Zn matrix via the particle stimulated nucleation DRX mechanism, resulting in finer microstructure of Zn-Mg-Ca alloy. Since the CaZn<sub>13</sub> particles could induce large stress concentration at their shape corners during deformation, which even causes crack of the particles in ECAP alloys, the ductility of Zn-Mg-Ca alloys is significantly deteriorated. Overall, the 12p ECAP Zn-Mg-Sr alloy exhibits optimal mechanical properties with ultimate tensile strength above 300 MPa and elongation higher than 20%. Nevertheless, the deformed Zn-Mg-Ca alloys possess poor ductility owing to the existence of CaZn<sub>13</sub> particles, which should be avoided in future design of Zn-based biodegradable metals.</p>
materials science, multidisciplinary,chemistry, physical,metallurgy & metallurgical engineering