Abstract:A seed-mediated method was employed here for CTAB-assisted gold nanoparticle growth. 3–4 nm silver aqueous colloid was stabilized by sodium citrate and used as seed solution to initial gold particle growth. The concentration of seed solution was calculated based on its relationship with silver atom concentration and seed particle statistical mean volume. It was found that there is a maximum seed concentration of 8.57 × 10−12 M (~25 µl 0.343 × 10−8 M seed solution added) in 10 ml 2.5 × 10−4 M HAuCl4 growth solution for growth of rodlike particles. Below this seed amount, the aspect ratio of nanorods could be controlled by varying the silver seed amount, i.e. nanorods with aspect ratio ~18.9 were obtained when the seed concentration in the growth solution was 0.343 × 10−12 M by adding 1 µl 0.343 × 10−8 M silver seed solution and nanorods with aspect ratio ~9.69 were obtained when the seed concentration in the growth solution was 1.715 × 10−12 M by adding 5 µl 0.343 × 10−8 M silver seed solution. As the seed concentration in the growth solution was more than 8.58 × 10−12 M (25 µl 0.343 × 10−8 M silver seed solution was added), there were no rodlike particles formed but spherical ones instead. These spheres were further studied by TEM and found to all be hollow structures. It was suggested that there were probably two different nucleation processes for growth of nanorods and spheres. For hollow spheres, the reaction between Ag seeds and Au ions formed hollow structures based on the Ag particle template effect. Then further growth of Au on these hollow structures produced hollow gold nanospheres. For nanorods, due to the very low concentration of silver seed (molar ratio of Ag seed: Au = 3.426 × 10−8), the growth process here probably was started by silver-induced Au nucleation, in which reduction of gold ions by silver resulted in small gold clusters. These gold clusters further grew up into nanoparticles and nanorods in the presence of CTAB.

Facile Fabrication of Caudate Gold Nanoparticles by A Temperature-Reducing Seeding Approach

Preparation of Nanochain and Nanosphere by Self-Assembly of Gold Nanoparticles

Synthesis of Gold Nanotadpoles by a Temperature-Reducing Seed Approach and the Dielectrophoretic Manipulation

One-step Seed-Mediated Growth of 30–150 Nm Quasispherical Gold Nanoparticles with 2-Mercaptosuccinic Acid As a New Reducing Agent

A Simple Method to Self-Assemble Two-dimensional and Three-dimensional Superlattices of Gold Nanoparticles

Seed-mediated Synthesis of Single-Crystal Gold Nanospheres with Controlled Diameters in the Range 5-30 Nm and Their Self-Assembly Upon Dilution.

Colloidal Gold Nanoparticle Formation Derived from Self-Assembled Supramolecular Structure of Cyclodextrin/au Salt Complex

Wet chemical synthesis of gold nanoparticles using silver seeds: a shape control from nanorods to hollow spherical nanoparticles

Formation mechanism of nonspherical gold nanoparticles during seeding growth: roles of anion adsorption and reduction rate.

Seed-Mediated Synthesis of Gold Nanorods at Low Concentrations of CTAB

Synthesis of Gold Colloid with Exclusion of Nonspherical Nanoparticles by Seeding Growth

Characterization of Gold Nanoparticles Synthesized Using Sucrose by Seeding Formation in the Solid Phase and Seeding Growth in Aqueous Solution

Formation and Stability of Gold Nanoflowers by the Seeding Approach: the Effect of Intraparticle Ripening

Size-Tunable Synthesis of Gold Nanorods Using Pyrogallol As A Reducing Agent

Seed‐Mediated Synthesis of Gold Nanobipyramids at Low CTAB Concentration Using Binary Surfactants

Facile Synthesis Of Gold Nanoplates By Citrate Reduction Of Aucl4- At Room Temperature

Facile synthesis of gold nanoflowers with high surface-enhanced Raman scattering activity

Porous gold nanobelts templated by metal-surfactant complex nanobelts.

Facile Controlled Preparation of Gold Nanoparticles with Amphiphilic Thiacalix[4]arene As Reductant and Stabilizer.

Atomically Precise Nanoclusters Predominantly Seed Gold Nanoparticle Syntheses.

Self-assembly of Cinnamic Acid-Capped Gold Nanoparticles