Elevated temperature initial permeability study of some ferromagnetic alloys

M.S. Leu,I-C. Tung,T.S. Chin

DOI: https://doi.org/10.1016/S0254-0584(98)00201-6

IF: 4.778

1998-01-01

Materials Chemistry and Physics

Abstract:An in situ measurement technique was designed to investigate temperature dependence of initial permeability (μi) for three soft magnetic materials: Ni79Fe16Mo5 Supermalloy, amorphous Co65Fe4Ni2Si15B14 alloy and nanocrystalline Fe73.5Cu1Nb3Si13.5B9 alloy. For the Ni79Fe16Mo5 Supermalloy, a small discrepancy on μi-T curve was observed between the heating and cooling processes and the Curie temperature (Tc) was obtained around 400°C in accordance with the Hopkinson effect. An annealing temperature at a value of ∼450°C is found sufficient to release the residual stress effect of the rewound core. For the amorphous Co65Fe4Ni2Si15B14 alloy, a very strong domain wall stabilization effect associating with a sharp valley on the μi-T curve at the temperature ranging from 110°C to 180°C is identified during the heating process. In addition, the Tc peak around 225°C obtained during heating matches that during cooling. For the Fe73.5Cu1Nb3Si13.5B9 alloy, the amorphous Tc value can be detected to be around 325°C during the heating process. However, during the cooling process two magnetic Curie transitions were found to be ∼581°C and 262°C corresponding to α-Fe (Si) nanocrystal and residual amorphous phase, respectively. The improvement in the room temperature μi value for the above materials can be achieved after in situ annealing studies.