Abstract:In order to obtain a steam-stable hydrogen permselectivity membrane, with tetraethylorthosilicate (TEOS) as the silicon source, zirconium nitrate pentahydrate (Zr(NO3)4·5H2O) as the zirconium source, and methyltriethoxysilane (MTES) as the hydrophobic modifier, the methyl-modified ZrO2-SiO2 (ZrO2-MSiO2) membranes were prepared via the sol-gel method. The microstructure and gas permeance of the ZrO2-MSiO2 membranes were studied. The physical-chemical properties of the membranes were characterized by Fourier transform infrared spectroscopy (FTIR), X-ray photoelectron spectroscopy (XPS), X-ray diffraction (XRD), transmission electron microscopy (TEM), scanning electron microscope (SEM), and N2 adsorption–desorption analysis. The hydrogen permselectivity of ZrO2-MSiO2 membranes was evaluated with Zr content, temperature, pressure difference, drying control chemical additive (glycerol) content, and hydrothermal stability as the inferred factors. XRD and pore structure analysis revealed that, as nZr increased, the MSiO2 peak gradually shifted to a higher 2θ value, and the intensity gradually decreased. The study found that the permeation mechanism of H2 and other gases is mainly based on the activation–diffusion mechanism. The separation of H2 is facilitated by an increase in temperature. The ZrO2-MSiO2 membrane with nZr = 0.15 has a better pore structure and a suitable ratio of micropores to mesopores, which improved the gas permselectivities. At 200 °C, the H2 permeance of MSiO2 and ZrO2-MSiO2 membranes was 3.66 × 10−6 and 6.46 × 10−6 mol·m−2·s−1·Pa−1, respectively. Compared with the MSiO2 membrane, the H2/CO2 and H2/N2 permselectivities of the ZrO2-MSiO2 membrane were improved by 79.18% and 26.75%, respectively. The added amount of glycerol as the drying control chemical additive increased from 20% to 30%, the permeance of H2 decreased by 11.55%, and the permselectivities of H2/CO2 and H2/N2 rose by 2.14% and 0.28%, respectively. The final results demonstrate that the ZrO2-MSiO2 membrane possesses excellent hydrothermal stability and regeneration capability.

Modified Zeolite Membrane Reactor for High Temperature Water Gas Shift Reaction

Effect of Hydrothermal Treatment on Suppressing Coking of Zsm-5 Zeolite During Methanol-To-Propylene Reaction

Low-temperature Cu/Zn/SBA-16 integrating carbon membrane reactor for hydrogen production and high CO conversion through water-gas shift reaction

Zeolite Membrane‐Based Low‐Temperature Dehydrogenation of a Liquid Organic Hydrogen Carrier: A Key Step in the Development of a Hydrogen Economy

Synthesis of Corrosion-Resistant MFI-type Zeolite Coatings by Solid-Conversion Secondary Growth Without Solvent

Intermediate-Temperature Reverse Water-Gas Shift Under Process Relevant Conditions Catalyzed by Dispersed Alkali Carbonates

MOF-derived Bimetallic Core-shell Catalyst HZSM-5@ZrO2-In2O3: High CO2 Conversion in Reverse Water Gas Shift Reaction

Development of A Combined Catalyst and Sorbent for the Water Gas Shift Reaction

Synthesis and Low-Temperature Detemplation of High-Silica Mfi Zeolite Membranes

Improved Synthesis of Hollow Fiber SSZ‐13 Zeolite Membranes for High‐Pressure CO2/CH4 Separation

Current progress on zeolite membrane reactor for CO2 hydrogenation

Highly Perm-Selective Micro-Porous Hydrotalcite-Silica Membrane for Improved Carbon Dioxide-Methane Separation

Modeling and Simulation of Water-Gas Shift Reactors with and without Membrane

Methanol Conversion to Dimethyl Ether in Catalytic Zeolite Membrane Reactors

Zirconia-Doped Methylated Silica Membranes Via Sol-Gel Process: Microstructure and Hydrogen Permselectivity

MOF-derived Bimetallic Core–shell Catalyst HZSM-5@ZrO2–In2O3: High CO2conversion in Reverse Water Gas Shift Reaction

Breaking the Permeability-Selectivity Trade-Off: Advanced carbon molecular sieve membranes derived from thermally rearranged Mixed-Matrix membrane precursors

Above‐Tg Annealing Benefits in Nanoparticle‐Stabilized Carbon Molecular Sieve Membrane Pyrolysis for Improved Gas Separation

Mixed-Matrix Organo–Silica–Hydrotalcite Membrane for CO2 Separation Part 2: Permeation and Selectivity Study

An active, stable cubic molybdenum carbide catalyst for the high-temperature reverse water-gas shift reaction

Low-temperature CO2 hydrogenation overcoming equilibrium limitations with polyimide hollow fiber membrane reactor