Abstract:Successive ion layer adsorption and reaction (SILAR) originally developed for the deposition of thin films on solid substrates from solution baths is introduced as a technique for the growth of high-quality core/shell nanocrystals of compound semiconductors. The growth of the shell was designed to grow one monolayer at a time by alternating injections of air-stable and inexpensive cationic and anionic precursors into the reaction mixture with core nanocrystals. The principles of SILAR were demonstrated by the CdSe/CdS core/shell model system using its shell-thickness-dependent optical spectra as the probes with CdO and elemental S as the precursors. For this reaction system, a relatively high temperature, about 220-240 degrees C, was found to be essential for SILAR to fully occur. The synthesis can be readily performed on a multigram scale. The size distribution of the core/shell nanocrystals was maintained even after five monolayers of CdS shell (equivalent to about 10 times volume increase for a 3.5 nm CdSe nanocrystal) were grown onto the core nanocrystals. The epitaxial growth of the core/shell structures was verified by optical spectroscopy, TEM, XRD, and XPS. The photoluminescence quantum yield (PL QY) of the as-prepared CdSe/CdS core/shell nanocrystals ranged from 20% to 40%, and the PL full-width at half-maximum (fwhm) was maintained between 23 and 26 nm, even for those nanocrystals for which the UV-vis and PL peaks red-shifted by about 50 nm from that of the core nanocrystals. Several types of brightening phenomena were observed, some of which can further boost the PL QY of the core/shell nanocrystals. The CdSe/CdS core/shell nanocrystals were found to be superior in comparison to the highly luminescent CdSe plain core nanocrystals. The SILAR technique reported here can also be used for the growth of complex colloidal semiconductor nanostructures, such as quantum shells and colloidal quantum wells.

Self-Assembly of Monolayers of Cadmium Selenide Nanocrystals with Dual Color Emission

Room Temperature Self-Assembly of CdSe Nanocrystals on SiO2-coated Si Wafer

Direct fabrication of monodispersed ultrasmall CdS nanocrystals from self-assembled monolayers on Au(111) substrate

Lateral Patterning of Luminescent CdSe Nanocrystals by Selective Dewetting from Self-Assembled Organic Templates

Self-Assembly of Semiconductor CdSe Nanocrystals by Bifunctional Linker Molecules

A Two-Step Synthetic Strategy Toward Monodisperse Colloidal Cdse and Cdse/Cds Core/Shell Nanocrystals

Printing and in Situ Assembly of CdSe/CdS Nanoplatelets As Uniform Films with Unity In-Plane Transition Dipole Moment

SELF-ASSEMBLY OF Ⅱ-Ⅳ COMPOUND NANOCRYSTALSON Si WAFER AT ROOM TEMPERATURE

Combinatorial Approaches Toward Patterning Nanocrystals

Hierarchical Luminescence Patterning Based on Multiscaled Self-Assembly.

Self-assembly of charged microclusters of CdSe/ZnS core/shell nanodots and nanorods into hierarchically ordered colloidal arrays

Patterning Of Self-Assembled Monolayers By Phase-Shifting Mask And Its Applications In Large-Scale Assembly Of Nanowires

Shape-Controlled Synthesis of SnE (E = S, Se) Semiconductor Nanocrystals for Optoelectronics

Large-scale Synthesis of Nearly Monodisperse CdSe/CdS Core/shell Nanocrystals Using Air-Stable Reagents Via Successive Ion Layer Adsorption and Reaction.

Lamellar Assembly of Cadmium Selenide Nanoclusters into Quantum Belts.

Molecular Patterning and Directed Self-Assembly of Gold Nanoparticles on GaAs

Microemulsion-Mediated Synthesis of Cadmium Zinc Sulfide Nanocrystals with Composition-Modulated Optical Properties

Facile synthesis of magic-sized CdSe and CdTe nanocrystals with tunable existence periods

Size-, Shape-, and Assembly-Controlled Synthesis of Cu2−xSe Nanocrystalsvia a Non-Injection Phosphine-Free Colloidal Method

Photoluminescent Colloidal Nanohelices Self-Assembled from CdSe Magic-Size Clusters via Nanoplatelets.

Preparation of Cadmium Selenide Nanocrystals Through an Ultrasonic Activation Double-Phase Approach at Room Temperature