Abstract:Alumina(Al2O3)sol was prepared by the sol-gel method using aluminium isopropoxide{Al[OCH(CH3)2]3}as primal raw material.Then porous SiC ceramic was used as matrix and coated by the dipping and drawing method.After the coated ceramic was heated,a compact Al2O3 coating was formed on the surface and the inner wall of the pores of the ceramic.Then the coated ceramic was insulated with fluid when it was used as a heating element.The scanning electron microscope photograph showed that the surface and the wall of the pores of the ceramic were coated by Al2O3 sol.The Al2O3 has good properties such as high dielectric constant and coefficient of resistance,inoxidizability and corrosion resistance,so the resistivity of coated ceramic was evidently increased.The higher resistivity can prevent the possibility that the fluid will be conducted.The Al2O3 coating also improved the inoxidizability of the SiC ceramic.The experimental results indicated that the percentage composition of Al2O3 coating is 43.1%in mass(the same below),and SiO2 and Si are 38.8%and 18.1%,respectively.The Al2O3 is the main composition of the coating,and SiO2 results from the oxidation of residual silicon.When the ceramic was sintered in the ihrigizing process,it was inevitable that some silicon would remain in the final ceramic.The residual silicon was oxidized when the ceramic was leaving the furnace and cooled in air,so the oxi-dization product SiO2 was left in the ceramic.The other part was produced during the heat treatment of the coating.Therefore,the content of SiO2 was higher.It is obvious from the above analysis that the Si came from the ceramic matrix.

Preparation and Properties of SiO_2-B_2O_3-MoSi_2-SiB_4 Coating for Ceramic Insulation Tile

High Emissivity MoSi2-SiC-Al2O3 Coating on Rigid Insulation Tiles with Enhanced Thermal Protection Performance

Microstructure and Properties of High Emissivity Coating for Fibrous Insulation Composites

High emissivity MoSi2–ZrO2–borosilicate glass multiphase coating with SiB6 addition for fibrous ZrO2 ceramic

Microstructure, radiative property and thermal shock behavior of TaSi2-SiO2-borosilicate glass coating for fibrous ZrO2 ceramic insulation

The Effects of Mineral Composition and Sintering Temperature on Synthetic Mullite

High emissivity MoSi2–TaSi2–borosilicate glass porous coating for fibrous ZrO2 ceramic by a rapid sintering method

Design, formation, and property of high emissivity WSi2-Si-glass hybrid coating on fibrous ZrO2 ceramic for reusable thermal protection system

Thermal Shock Behavior and Infrared Radiation Property of Integrative Insulations Consisting of MoSi2/borosilicate Glass Coating and Fibrous ZrO2 Ceramic Substrate

Effects of Coating on Performance Rigid Tile

RESEARCH ON HIGH-EFFICIENT THERMAL INSULATION CERAMIC MATERIALS

INSULATION COATING ON ELECTRO-HEATING POROUS SILICON CARBIDE CERAMIC

Evolution of Microstructure and Radiative Property of Metal Silicide–glass Hybrid Coating for Fibrous ZrO2 Ceramic During High Temperature Oxidizing Atmosphere

Fabrication of Dense Β-Si3n4-based Ceramic Coating on Porous Si3N4 Ceramic

A high emissivity coating with a sacrificial interface layer on ceramic fiber fabric for high temperature application

High-temperature Melt-Infiltration Preparation and Erosion Behavior of Γ-Y2si2o7 /Y2o3-Sio2-al2o3 Glass Coating on Porous Si3N4 Ceramics

Prepration and Thermal Shock Resistance Property Ofγ-Y2 Si2 O7 Ceramic Coating on Surface of Porous Silicon Nitride

The influence of sodium silicate water glass content on the structure and properties of silicate thermal insulation coating

Fabrication and Thermal Shock Resistance of Multilayer Γ-Y2si2o7 Environmental Barrier Coating on Porous Si3N4 Ceramic

Preparation and Thermal Shock Resistance of High Emissivity Molybdenum Disilicide- Aluminoborosilicate Glass Hybrid Coating on Fiber Reinforced Aerogel Composite

Fabrication of a Novel MgO-B2O3-SiO2-Zn Coating by Thermal Spraying