Abstract:Nanostructured and conventional alumina–3 wt.% titania monolithic coatings were deposited by air plasma spraying (APS). The thermal diffusivity was measured by the laser flash technique. The thermal diffusivity of the nanostructured Al2O3–3 wt.% TiO2 coating was higher compared with that of the corresponding conventional coating at temperature ranging from 200 to 1000 °C. For the nanostructured coating, there was no difference in the thermal diffusivity between during heating and cooling. However, the thermal diffusivities of the conventional coating were higher during cooling than those during heating. SEM and TEM examination showed that the nanostructured coating contained equiaxed grains with sizes from 150 to 800 nm besides splat lamellae. In the nanostructured coating, most of columnar grains in splat lamellae were less than 200 nm. Splat lamellae of the nanostructured coating bonded well each other and their thickness ranged from 0.4 to 1 μm. The decrease of thermal diffusivity of the nanostructured coating was attributed to the increase of grain boundaries and defective crystal structure. The stability of thermal diffusivity of the nanostructured coating was considered to relate to the absence of narrow long micro-cracks between splat lamellae. Nanostructured and conventional alumina–3 wt.% titania monolithic coatings were deposited by air plasma spraying (APS). The thermal diffusivity was measured by the laser flash technique. The thermal diffusivity of the nanostructured Al2O3–3 wt.% TiO2 coating was higher compared with that of the corresponding conventional coating at temperature ranging from 200 to 1000 °C. For the nanostructured coating, there was no difference in the thermal diffusivity between during heating and cooling. However, the thermal diffusivities of the conventional coating were higher during cooling than those during heating. SEM and TEM examination showed that the nanostructured coating contained equiaxed grains with sizes from 150 to 800 nm besides splat lamellae. In the nanostructured coating, most of columnar grains in splat lamellae were less than 200 nm. Splat lamellae of the nanostructured coating bonded well each other and their thickness ranged from 0.4 to 1 μm. The decrease of thermal diffusivity of the nanostructured coating was attributed to the increase of grain boundaries and defective crystal structure. The stability of thermal diffusivity of the nanostructured coating was considered to relate to the absence of narrow long micro-cracks between splat lamellae.

Microstructure of alumina–3wt.% titania coatings by plasma spraying with nanostructured powders

The Microstructure of Al2O3/TiO2-NiCrBSi Graded Thermal Barrier Coatings Produced by Flame Spraying

Characterization of Alumina–3 Wt.% Titania Coating Prepared by Plasma Spraying of Nanostructured Powders

Influence of Composite Powders’ Microstructure on the Microstructure and Properties of Al2O3–TiO2 Coatings Fabricated by Plasma Spraying

D. C. Plasma-Sprayed Coatings of Nanostructured Alumina-Titania-Silica

Thermal diffusivity of plasma sprayed monolithic coating of alumina–3 wt.% titania produced with nanostructured powder

Fabrication and Evaluation of Plasma Sprayed Nanostructured Alumina–titania Coatings with Superior Properties

Microstructure, adhesion, microhardness, abrasive wear resistance and electrical resistivity of the plasma sprayed alumina and alumina–titania coatings

Microstructure & Tribological Performance of Alumina-3wt% Titania Coatings Produced by APS

The dependency of microstructure and properties of nanostructured coatings on plasma spray conditions

Microstructure and Properties of Multi-Function Micro-Plasma Sprayed Al2o3 Coatings

Microstructure, spallation and corrosion of plasma sprayed Al2O3–13%TiO2 coatings

Microstructure and Properties of Al_2O_3-13wt%TiO_2 Coatings Fabricated by Plasma Spraying and Laser Remelting on Titanium Alloy

Abrasive wear characteristics of plasma sprayed nanostructured alumina/titania coatings

Microstructure And Properties Of Nano-Structured Al2o3-13%Tio2 Coating By Aps

Mechanical structure and property analysis of Al_2O_3-13%TiO_2 nano-structured plasma sprayed coatings

Toughening and Strengthening Mechanism of Plasma Sprayed Nanostructured Al2O3–13 Wt.%tio2 Coatings

Improving microstructure and properties by multi-function micro-plasma spraying

Microstructure and properties of Al2O3–ZrO2–TiO2 composite coatings prepared by plasma spraying

Properties of multi-function micro-plasma sprayed nanostructured Al 2O3-13wt%TiO2 coatings