Second Phase Strengthening and Grain Boundary Segregation Effects on the Microstructure and Properties of (Ce, Y)-TZP-Based Ceramics Prepared by Vat Photopolymerization
Ren-Zhong Zhang,Yu-Xuan Huang,Wei-Kang Li,Yu Luo,Ming-Zhu Pan,Jia-Min Wu,Xiao-Yan Zhang,Chun-Sheng Ye,Yu-Sheng Shi
DOI: https://doi.org/10.1016/j.addma.2024.104482
IF: 11
2024-10-19
Additive Manufacturing
Abstract:Immediate implant placement (IIP) has garnered significant attention due to its minimally invasive approach and ability to facilitate immediate crown replacement. Nevertheless, challenges persist in processing complex geometries and selecting suitable materials. This study successfully fabricated high-performance, complex-structured (Ce, Y)-TZP-based composite ceramics using vat photopolymerization (VPP) technology, combining second-phase strengthening and grain boundary segregation effects. The incorporation of α-Al 2 O 3 as a secondary phase led to a progressive refinement of (Ce, Y)-TZP grains, with the most favorable grain size achieved at 20 wt% α-Al 2 O 3 , reducing the average grain size to 0.75 μm. However, excessive α-Al 2 O 3 content resulted in micropore formation, compromising the material's mechanical performance. At an optimal concentration of 15 wt% α-Al 2 O 3 , the composite exhibited superior mechanical properties, including a Vickers hardness of 11.53 ± 0.27 GPa and a flexural strength of 525.5 ± 21.3 MPa. Despite these improvements, some coarse (Ce, Y)-TZP grains persisted within the ceramic matrix. To further enhance grain refinement at lower α-Al 2 O 3 content, a minimal addition of La 3+ (0.1 wt%) was introduced, promoting grain boundary segregation and additional grain refinement. This modification reduced the (Ce, Y)-TZP grain size to 0.74 μm, increased hardness to 13.03 ± 0.31 GPa, and elevated flexural strength to 550.4 ± 39.8 MPa, while maintaining excellent material stability.
engineering, manufacturing,materials science, multidisciplinary