Abstract:Nanosized copper oxide-zirconia particles containing 10-30 mol% of copper were prepared by using a precipitation technique in aqueous tetramethylammonium hydroxide solutions. Two methods, in situ (INS) and step-by-step (SBS), which differed in the time when the copper salt was introduced to the synthesis procedure, were used, and this allowed a comparison of the properties of the final powders produced using the two modes of preparation. The surface areas and phase compositions were different for the samples prepared from the two different methods after calcination at 500 degreesC. A surface area of 168 m(2) g(-1) was obtained for the sample prepared with the SBS method and 121 m(2) g(-1) for the INS method, both contain 30 mol% copper. Tetragonal ZrO2 was observed from X-ray diffraction patterns for all samples prepared with the SBS method, however, no separate phase of copper or copper oxide was observed. It is proposed that all of the copper is finely distributed on the surface of the ZrO2 particles with the SBS method. For the samples prepared from the INS method, tetragonal ZrO2 was obtained at a low copper content and the peaks indexed to tetragonal ZrO2 shifted to higher angle with the increase of copper content, indicating copper ions being incorporated into the lattice. An amorphous compound was obtained at high copper content (30 mol%). The phase change with the calcination temperature was also investigated for the INS sample containing 30 mol% copper. The studies show that tetragonal ZrO2 and copper oxide were present after calcination at 400 degreesC, and tetragonal ZrO2 with a small amount of monoclinic ZrO2, as well as copper oxide, formed after calcination at 700 degreesC. However, after heating at 500 degreesC, amorphous compounds were obtained, suggesting that 500 degreesC could be a phase transition point. The incorporation of copper in the ZrO2 lattice resulted in a loss of order in the ZrO2 structure when calcined at 500 degreesC, with a further increase in the calcination temperature leading to the phase change.

Uv Raman Spectroscopic Study on the Surface Phase of Zro2 Modified with Nd2o3

Uv Raman Spectroscopic Study on the Phase Transformation of Zro2, Y2o3-Zro2 and So42-/Zro2

Phase Transformation in the Surface Region of Zirconia and Doped Zirconia Detected by UV Raman Spectroscopy

Preparation of Y2o3 Stabilised Zro2 Ceramic Nanopowders by Surface Doping

Texture and Surface Morphology Effects on Tetragonal Phase Stabilization in Zro2 Films Deposited by Metal-Organic Chemical Vapor Deposition

Study of Influence of Calcination Atmosphere on Phase Transformation of Zirconia by UV Raman Spectroscopy

Effect of Nd2O3 Addition on the Surface Phase of TiO2 and Photocatalytic Activity Studied by UV Raman Spectroscopy

Doping and Grain Size Effects in Nanocrystalline ZrO2–Sc2O3system with Complex Phase Transitions: XRD and Raman Studies

Surface-Enhanced Raman Scattering Activity of ZrO2 Nanoparticles: Effect of Tetragonal and Monoclinic Phases

Effects of Zr Doping on the Surface Energy and Surface Structure of UO2: Atomistic Simulations

Effect of dopant loading and calcination conditions on structural and optical properties of ZrO2 nanopowders doped with copper and yttrium

Facile Synthesis and Characterization of ZrO₂ Nanoparticles via Modified Co-Precipitation Method

Preparation and characterization of CuO–ZrO2 nanopowders

The Surface Modification of ZrO2 Film by Zr/Nb Ion Implantation and First-Principles Calculation

The Stabilization Mechanism and Size Effect of Nonpolar-to-polar Crystallography Facet Tailored ZnO Nano/micro Rods Via a Top-Down Strategy.

Optimization of the structure and morphology of monoclinic phase nanoscale zirconium dioxide

Surface modification of ZrO2 nanopowder with oxovanadium species using slurry deposition and impregnation methods

Thermal stability and photoluminescence of Zr1−xCexO2 (0≤x≤1) nanoparticles synthesized in a non-aqueous process

Unusual Calcination Temperature Dependent Tetragonal–monoclinic Transitions in Rare Earth-Doped Zirconia Nanocrystals

[Vibrational spectrum and XPS contrastive studies on pyrochlore-type oxygen-rich Ce2Zr2O8 and oxygen-defective Nd2Zr2O7 phases]

Co-precipitation of nano Mg–Y/ZrO2 ternary oxide eutectic system: Effects of calcination temperature