Experimental study of bonding strength between resin composite direct core build-up materials and dentin in vitro
Yu Changlu,Chen Meimei,Ye Maochang
DOI: https://doi.org/10.3969/j.issn.1000-0399.2012.08.013
2012-01-01
Abstract:Objective To compare the microtensile bonding strength between two resin composite direct core build-up materials and dentin prepared with a superfine-grit diamond bur when using three different dentin adhesives.Methods Two kinds of resin composite core build-up materials,Bisfil-core and Luxacore,and three kinds of adhesives,ONE-STEP○RPLUS,Contax and ibond,were used in this study.The six corresponding groups were BO,LO,BC,LC,Bi,Li,respectively.Eighteen human molarswere randomly divided into six groups with three teeth in each group in this study.The coronal enamel of all teeth was removed and the superficial dentin was exposed,which were then prepared with a superfine-grit diamond bur.The dentin adhesives were applied to dentin surface according to manufacturers' instructions.The teeth were then restored with two resin composite direct core build-up materials and stored in tap water at 370C for 24 hours.After that,the teeth were sectioned perpendicular to the bonded surface into slices approximately 0.7mm thickness.Each slice was then trimmed into an hourglass shape to provide a 1.0 mm2 bonded area.The specimens were subjected to microtensile bond strength testing on MTS Synergie100 testing machine.Data were analyzed by ANOVA and LSD test.Results Bonding strength of each group as follows: BO(927.34±6.52)MPa,LO(36.49±11.74) MPa,BC(23.78±9.03)MPa,LC(34.35±13.35)MPa,Bi(29.12±7.99)MPa,Li(32.63±8.17)MPa.The difference is not significant in dentin adhesives but significant in resin composite direct core build-up materials.Conclusion All three dentin adhesives can meet the demand of clinical practice.A flowable resin composite core material can enhance the bonding strength significantly.