Dynamic Recrystallization Behavior of Biomedical CCM Alloy with Additions of C and N

Yui Yamashita,Yunping Li,Emi Onodera,Hiroaki Matsumoto,Akihiko Chiba
DOI: https://doi.org/10.2320/matertrans.MAW201007
2010-01-01
MATERIALS TRANSACTIONS
Abstract:In order to examine the dynamic recrystallization (DRX) behaviors of Co-29Cr 6Mo alloy with additions of both C and N (hereafter CCMCN alloy) uniaxial compression tests in the temperature, range of 1273 to 1473 K and strain rates of 0 01 to 30s(-1) were carried out The influence of hot forging conditions (i e , temperature strain rate and strain) on the microstructure of deformed sample was investigated in detail by means of electron backscattering diffraction (EBSD) and optical microscopy (OM) The results revealed that the initial microstructure is a stable gamma face centered cubic (FCC) phase with a large number of M23C6 precipitates both inside the grains and at grain boundaries The DRXed grains were observed to be uniformly distributed and to decrease with strain The high volume fraction of Sigma 3 boundaries after the DRX was observed indicating a close relation between die DRX mechanism and Sigma 3 boundary) formations In addition, the activation energy Q of CCMCN alloy was observed to be higher as compared to those of alloys without C or N addition and that with N addition [doi 10 2320/matertrans MAW201007]
What problem does this paper attempt to address?