Abstract:The chemical heat sink yielded by the catalytic cracking of supercritical hydrocarbons facilitates the thermal management of hypersonic aircraft. The objective of this study was to alleviate the diffusion restriction of supercritical hydrocarbons in conventional microporous zeolite films. A dual template method involving different n (C22-6-6)/n (TPAOH) values was adopted to prepare pillared nanosheet HZSM-5 zeolite films by using seed assisted secondary growth. Compared with those of the parent nanosheet HZSM-5 zeolite film (ZN) prepared using only C22-6-6 as the structure directing agent (SDA), the zeolite film prepared using n (C22-6-6)/n (TPAOH) of 10/4 (DZN-4) after pillaring exhibited a higher surface area (525 m2 g−1) and mesoporous volume (0.453 cm3 g−1). A larger amount of TPAOH in the synthesized solution (n (C22-6-6)/n (TPAOH) < 10/6) induced the formation of a bulky microporous MFI crystal phase, thereby sacrificing the mesoporous structure. At 550 °C and 4 MPa, the DZN-4 zeolite film yielded the highest n-dodecane conversion rate (76.8%) and TOF value (130.9 s−1), due to the presence of highly accessible Brønsted acid sites and ordered mesoporous structures, leading to a heat sink of 2.99 MJ kg−1, which is 32% higher than that under ZN. Restricted secondary reactions, such as hydride transfer and aromatization, were observed in the presence of highly connected mesopores designed by pillaring, leading to high and low selectivities toward olefins and aromatic compounds, respectively. Amorphous coke was detected on the external mesopore surface of DZN-4, and the adhesive strength was significantly enhanced, resulting in a higher catalytic stability.

Experimental evidence for the enhanced cracking activity of n-heptane over steamed ZSM-5/mordenite composite zeolites

Influence of steam treatment on ZSM-5 catalyst and MTP reaction

ZSM-5 Crystals Grown on the Wall of a Long Tubular Reactor As a Structured Catalyst for Cracking of Endothermic Fuels

Effect of Hydrothermal Treatment on Suppressing Coking of Zsm-5 Zeolite During Methanol-To-Propylene Reaction

Preparation and Catalytic Properties of ZSM-5 Zeolite Films on FeCrAl Alloy Grids

Effect of Hierarchical ZSM-5 Zeolite Crystal Size on Diffusion and Catalytic Performance of N-Heptane Cracking

Nanometer β Zeolite Made from Mesoporous Zeolite and Its Hydrocracking Performance

ZSM-5@MCM-41 core–shell composite with tunable shell thickness for n -heptane catalytic cracking reaction

Effects of post treatment of HZSM-5 zeolites on catalytic cracking of butene

Dealumination Kinetics of Composite ZSM-5/mordenite Zeolite During Steam Treatment: an In-Situ DRIFTS Study

Effect of Particle Size of Single-Crystalline Hierarchical ZSM-5 on Its Surface Mass Transfer in N-Heptane Catalytic Cracking

Insight into performance over IM-5, ZSM-5 and ZSM-11 zeolites for n -heptane cracking to light olefins in the absence & presence of steam

Catalytic Cracking of Supercritical N-Dodecane over Meso-Hzsm-5@al-mcm-41 Zeolites

The Influence of External Acid Strength of Hierarchical ZSM-5 Zeolites on N-Heptane Catalytic Cracking

The influence of pore-architecture over n -heptane cracking using MFI, *BEA and MSE zeolite catalysts: Multipore versus hierarchical porosity

ZSM–5@KIT–6 encapsulated composite molecular sieves for the catalytic cracking of waste cooking oil model compound to produce light olefins

n-Heptane catalytic cracking on ZSM-5 zeolite nanosheets: Effect of nanosheet thickness

Synthesis of pillared nanosheet HZSM-5 zeolite films for catalytic cracking of supercritical n-dodecane

Steam catalytic cracking and lump kinetics of naphtha to light olefins over nanocrystalline ZSM-5 zeolite

Effects of the controllable mesostructure of nano-sized ZSM-5 on the co-cracking of phenolic bio-oil model compounds and ethanol

Preparation of nano ZSM-5 with hydrophobic surfaces and application to catalytic cracking of hydrocarbon fuels