Photoluminescence Properties of La3PO7:Eu3 + Nanoparticles Synthesized by a Combustion Method
JIN Ye,QIN Wei-ping,ZHANG Ji-sen,WANG Yan,CAO Chun-yan,ZHANG Ji-shuang,REN Xin-guang,ZHU Pei-fen,WEI Guo-dong,WANG Li-li,WANG Guo-feng
DOI: https://doi.org/10.3321/j.issn:1000-7032.2007.02.014
2007-01-01
Abstract:Eu3+-doped oxyphosphate (La3PO7) nanoparticles were synthesized by a straightforward combustion method. The synthesis procedure is similar to that of preparing oxide nanomaterials by the combustion method, but here (NH4)2HPO4 is used in producing phosphate nanoparticles. Firstly, La(NO3)3 was prepared by putting appropriate molar rate La2O3 (1.5 mmol) and Eu2O3 into the thin HNO3, stirring to a transparent solution. Excess water was evaporated and made it condensed while heating to obtain the solid La(NO3)3. Then, put into 10 mL thin HNO3. At the same time, 0.1321 g (NH4)2HPO4 and 0.270 3 g Glycine were dissolved in deioned water (10 mL). Thirdly, the solution of (NH4)2HPO4 and glycine were added into that of the La(NO3)3 with vigorous stirring. The precursor solution was formed. Then, the precursor solution was heated until the white foam was obtained. The reaction took place in a few minutes and all the reactions happened in a wide-mouth beaker. A monoclinic lattice was verified in them by the investigation of X-ray diffraction (XRD). In the emission spectra of Eu3+, the 5D0→7F0 transition is often observed when Eu3+ is in low site symmetry because it is forbidden based on the group theory. The 5D0→7F1 transition is parity-allowed magnetic dipole transition, which is slightly affected by the symmetry of the Eu3+ site. The 5D0→7F2 transition is a parity forbidden electric dipole transition and strong emission only occurs in a non-inversion symmetry site. Under 254 nm excitation, La3PO7∶Eu3+ nanoparticles emitted mainly red fluorescence, assigned to the 5D0→7F2 transition of Eu3+ ions and revealed the Eu3+ ions occupied asymmetric sites in the oxyphosphate host. After annealing at different temperatures from 400 ℃ to 1 200 ℃, we found that the higher the annealing temperature, the better the samples crystallized and the bigger the intensity ratio of I(5D0-7F2)/I(5D0-7F1). In comparison with LaPO4∶Eu3+, an orange phosphor with stronger 5D0→7F1 emission, La3PO7∶Eu3+ has prominent red luminescence under the same excitation and maybe become a promising red phosphor for PDPs and Hg-free fluorescent lamp in the future.