The Preparation of CaO∶Eu3+, Li+ Red Phosphor Powder

Ming KANG,Guang-fu YIN,Xiao-ming LIAO,Jun LIU,Rong SUN

2009-01-01

Abstract:CaCO3 was chosen as main raw material,and wet chemical method was used for the preparation of precursor.According to TG-SDTA analysis,the precursor was directly calcined at 850 ℃ for 2 h to obtain CaO∶Eu3+,Li+.The structure,morphology and spectra properties of the samples were characterized by XRD,laser particle size analyzer,SEM,FT-IR,Raman,UV and PL-PLE spectra,respectively.The results showed that the Eu3+ ions as a luminescent center substituted Ca2+ ions into the lattice,and the cubic CaO structure could be maintained.Li+ ion as sensation was helpful to the energy transfer between O2-and Eu3+,and could enhance the luminescence.The size of particles was 0.5~1.0 μm.The obtained sample could emit the light with the wave length of 592 nm(5D07F2) under the radiation of the ultraviolet light with the wavelength of 244 nm,which indicated that Eu3+ ions mainly located in strict symmetric position of the crystal lattice and belonged to red luminescence.