Study on luminescence of CaLaAl3O7:Eu3+ phosphor

Deyin Wang,Yuhua Wang

DOI: https://doi.org/10.3321/j.issn:1002-185x.2006.12.021

2006-01-01

Rare Metal Materials and Engineering

Abstract:CaLa1-xAl3O7:xEu(3+) (0 <= x <= 1)phosphors were synthesized by nitrate pyrogenation reaction and their luminescence properties were investigated. XRD results showed that in the range of 0 <= x <= 1, CaLa1-xAl3O7:xEu(3+) were formed as good single phase, indicating no change occurred in its crystal structure. Under 254 nm UV excitation, the CaLa1-xAl3O7:xEu(3+) phosphor exhibited the well-known Eu3+ emission, which made up of several sharp lines dominated by 616nm, and its 616nm (D-5(0)-> F-7(2)) emission intensity reached its maximum at x=0.2. Under 147 nm excitation, its emission spectra was consistent with that of 254 nm UV excitation, and reached its maximum at x=0.2, but its emission intensity was much weaker than that of 254 nm UV excitation, which implied that the luminescent mechanism under UV excitation was different from that under 147 urn VUV excitation.