Chromatographic Separation of Strontium (II) from a Nitric Acid Solution Containing Some Typically Simulated Elements by a Novel Silica‐Based TODGA Impregnated Polymeric Composite in the MAREC Process
AY Zhang,YZ Wei,H Hoshi,M Kumagai
DOI: https://doi.org/10.1081/sei-200049894
2005-01-01
Solvent Extraction and Ion Exchange
Abstract:A new kind of macroporous silica-based N,N,N',N'-tetraoctyl-3-oxapentane-1,5-diamide (TODGA) chelating polymeric adsorption material (TODGA/SiO2-P) was developed and synthesized by impregnating TODGA molecules into the pores of similar to 50 mu m SiO2-P particles to separate strontium effectively from high-level liquid waste (HLLW). The adsorption of some typically simulated elements Na(I), K(I), Cs(I), Rb(I), Sr(II), Ba(II), and Ru(III) towards TODGA/SiO2-P adsorbent was investigated by examining the influence of contact time and HNO3 concentration. It was found that with an increase in the HNO3 concentration, the adsorption of Sr(H) onto TODGA/SiO2-P adsorbent increased quickly from 0.5 M to 2.0 HNO3 and then decreased. TODGA/SiO2-P exhibited excellent adsorption ability and selectivity for Sr(II) over all of the tested elements, which showed almost no adsorption. Based on the batch experiments, the separation of Sr(II) from a 2.0 M HNO3 solution containing similar to 5 x 10(-3) M of the simulated elements was performed by TODGA/SiO2-P packed column at 25 degrees C and 50 degrees C, respectively. Cs(I), K(I), Ru(III), Ba(III), Rb(I), and Na(I) were found to facilely elute out column and flow into effluent along with feed solution and 2.0 M HNO3 because of no adsorption. Sr(II) adsorbed towards TODGA/SiO2-P was desorbed sufficiently by distilled water and separated completely from the simulated elements. Its recovery percentage was 100.2% at 25 degrees C and 99.7% at 50 degrees C. Furthermore, the leakage behavior of TODGA from its silica-based adsorbent was investigated. It was found that the quantity of TODGA leaked was basically equivalent to its solubility in the corresponding HNO3 solution.