Formation of AlNi Phase and Its Influence on Hydrogen Absorption Kinetics of Mg77Ni23-xAlx Alloys at Intermediate Temperatures
Wenchao Cao,Xin Ding,Yong Zhang,Jiaxin Zhang,Ruirun Chen,Yanqing Su,Jingjie Guo,Hengzhi Fu
DOI: https://doi.org/10.1016/j.ijhydene.2022.06.022
IF: 7.2
2022-01-01
International Journal of Hydrogen Energy
Abstract:In order to reduce the obstacle influence of coarse Mg2Ni phase on hydrogen absorption kinetics in Mg-Ni alloys, aluminum was doped and Mg22Ni23-xAlx (x = 0, 3, 6, 9) alloys were prepared. The results show that AlNi phase was formed when Al was added, the size of primary Mg2Ni phase decreases with increasing Al content till 6 at.%, while primary Mg2Ni phase was diminished and primary Mg phase was formed when Al content increased to 9 at.%. The initial hydrogenation rates of Mg22Ni23-xAlx alloys were increased, which is resulted from the refined primary Mg2Ni and the catalytic AlNi phase. More importantly, the hydrogenation rates and capacities were significantly improved at 150 degrees C, especially for the Mg(22)Ni(12)Al(6)( )alloy. The apparent activation energy of the Mg22Ni12Al6 alloy for hydro- genation was reduced to 73.68 kJ/mol from 102.27 kJ/mol of the Mg77Ni23 alloy. Its enthalpy changes for hydrogenation at low and high platforms are 72.3 kJ/mol and 53.9 kJ/mol, respectively. The multiple channels and short distance for hydrogen atoms diffusion provided by refined primary Mg2Ni phase, the solid dissolution of Al in Mg2Ni lattice, and catalytic effect of AlNi on hydrogenation, leading to the improvement of the hydrogen storage properties. (C) 2022 Hydrogen Energy Publications LLC. Published by Elsevier Ltd. All rights reserved.