Abstract:OBJECTIVE:To evaluate the F(-) releasing and recharging properties of six dental restorative materials. METHODS:Disc specimens 10 mm in diameter and 1 mm in thickness were prepared from 6 different dental restorative materials: Fuji VII [glass ionomer cement (GIC)], Fuji II LC (light-curing, GIC), Beautifil (giomer), Compoglass F (compomer), Charisma (composite) and Experimental I (a fluoride releasing composite), with 10 discs for each material. Specimens were dipped in 5 ml deionized water and F(-) release was detected using a fluoride-specific ion electrode every day from 1-7 days and every three days from 8-28 days. On day 28, specimens were exposed to a fluoride foam for 4 min and then dipped in water, then the F(-) concentration was detected every day for a week. The specimens were exposed to fluoride foam and fluoride release was detected repeatedly for three times. RESULTS:All materials presented the highest F(-) release on the first day after dipping and the F(-) release sharply decreased after 24 h and slowly decreased after 3 days. On the first day, Fuji VII presented the highest F(-) release[(99.68±15.21) µg×cm(-2)×d(-1)], followed by Fuji II LC [(37.12±1.67) µg×cm(-2)×d(-1)], Experimental I [(22.93±1.53) µg×cm(-2)×d(-1)], Compoglass F[(15.28±0.70) µg×cm(-2)×d(-1)], Beautifil[(2.40±0.52) µg×cm(-2)×d(-1)] and Charisma[(0.11±0.02) µg×cm(-2)×d(-1)]. Within 28 days of dipping, both Fuji VII and Fuji II LC released more F(-) than other materials did(P < 0.05), followed by Compoglass F and Experimental I, and Beautifil and Charisma released the least F(-)(P < 0.01). After F(-) uptake, all materials released the highest F- on the first day and presented sharply decrease after 24 h and slowly decrease after 2 days. On the first day after F(-) uptake, Fuji VII presented the highest F(-) release (>40 µg×cm(-2) ×d(-1)), much more than other materials(P < 0.01), followed by Fuji II LC(>25 µg×cm(-2) ×d(-1)). Beautifil, Compoglass F and Experimental I were close in F(-) release value(15- 20 µg × cm(-2) × d(-1)), and Charisma showed the lowest F(-) release. CONCLUSIONS:Two glass ionomers were shown to have highest capacity in F(-) release and uptake, followed by compomer and fluoride releasing composite. Composite demonstrated the lowest F(-) release and uptake and Giomer was comparable to composite in F(-) release and to compomer and fluoride releasing composite in F(-) uptake.

Comparison of Fluoride Release from Glass-ionomer Cements and a Compomer in Vitro.

Effects of Incorporation of Nano-Fluorapatite or Nano-Fluorohydroxyapatite on a Resin-Modified Glass Ionomer Cement

Clinical evaluation of glass ionomer and resin-based sealant on partially erupted permanent first mo-lars

Fluoride Release and Recharge Ability of A Novel Fluoride Release Composite Resin

Fluoride release and uptake by glass-ionomers and related materials and its clinical effect

[Fluoride Release and Recharge Properties of Six Restorative Materials].

Evaluation and Comparison of Fracture Strength and Fluoride Releasing Properties of New Alkasite Materials with Conventional Restorative Material, Bulk Fill Composite and Glass Ionomer Cement: An In-Vitro Study

In vitro comparative fluoride release, and weight and volume change in light-curing and self-curing glass ionomer materials

Comparative Evaluation of the Fluoride Releasing Ability and Microbial Attachment of Glass-Hybrid Restorative Material

Comparation of the Clinical Effects of Glass Ionomer Cement and Flowable Composite Resin on the Restoration of Dental Wedge-Shaped Defects

Evaluating the Mechanical Properties of Restorative Glass Ionomers Cements

Inhibitive Effect of a New Dental Resin Composite on Enamel Artificial Caries

Comparative study of two bioactive dental materials

In vitro comparison of bonding to zirconia- or glass- based ceramics between flowable resin composites and composite resin cements

The influence of light‐curing time on fluoride release, surface topography, and bacterial adhesion in resin‐modified glass ionomer cements: AFM and SEM in vitro study

Effect of a novel glass ionomer cement containing fluoro-zinc-silicate fillers on biofilm formation and dentin ion incorporation

Characterization of a novel light-cured star-shape poly(acrylic acid)-composed glass-ionomer cement: fluoride release, water sorption, shrinkage, and hygroscopic expansion

Fluoride release from aged resin composites containing fluoridated glass filler

Comparison of remineralization ability of tricalcium silicate and of glass ionomer cement on residual dentin: an in vitro study

Mechanical Properties and Ion Release from Fibre-Reinforced Glass Ionomer Cement

Comparative evaluation of microleakage between bulk esthetic materials versus resin-modified glass ionomer to restore Class II cavities in primary molars