Abstract:BACKGROUND:Polylactic acid(PLA)surface is hydrophobic and there are no nataral recognition sites,so its application is limited.Many different strategies have been studied such as composition and chemical Drafting,to produce hydrophilic groups.However,these traditional methods are always involved in complex process and many organic reagents,resulting in decrease of biocompatibility.OBJECTIVE:To conduct the surfacr modification of PL.A and improve its hydrophilicity with low temperature plasma treatment.DESIGN:Controlled observation.SETTING:Department of Materials Science and Engineering in Jinan University.MATERIAIS:The experiment was processed from October 2004 to October 2005 at Guangzhou Research Center of Artificial Organs and Materials Engineering(Ministry of Education).The mainly used materials were:Poly-D,L-lactic acid(Mr 2.9×104,Shandong Medical Instrument Institute),N-vinyl-pyrrolidone(NVP,Acros Company,purified before use).METHODS:The materials were treated in the plasma reactor under different conditions(power=150 W,t=3,2,1 minutes;power=30 W,t=10,8,5,3,1 minutes)to choose the optimal condition,and then PLA were grafted with NVP by gas phase polymerization and liquid polymerization,respectively.MAIN OUTCOME MEASURES:THe surface morphology of the films was observed with scanning electron microscopy and atomic force microscopy.The hydrophilicity of native and treated material surfaces was measured using a water contact angle meter.Surface composition was detected with Fourier transform infrared spectrometer.Mass changesmeasurement was applied to characterize the grafting efficiency.RESULTS:Scanning electron microscopy and atomic force microscopy showed that the plasma medified materials possessed coarse surface with pores and notches.Water contact angles decreased obviously from 78°to 50°after grafting,Fourier transform infrared spectrometer showed a new absorption peak at 1 637.19 cm-1,which corresponded to the carbonyl stretch vibration absorption of amide group in poly-N-vinyl-pyrrolidone.After the plasma treatmerlt at low temperature.the mass change ratio of PLA film material was-0.6.CONCLUSION:The plasma treatment and polymerization can improve the hydrophilicity and cause coarsr surface of PLA material,which will be helpful for the cell attachment.

Surface modification of poly-D,L-lactic acid film with plasma graft polymerization

Plasma Induced Graft Polymerization of NVP on PLA Surface

Surface Modification of Polylactic Acid by UV-Irradiation and Its Cytocompatibility

Treatment of Poly-L-Lactic Acid Surface by Ammonia Plasma to Promote the Osteoblast Compatibility

Surface Modification of Biodegradable Poly(D,L-Lactic Acid) by Nitrogen and Nitrogen/Hydrogen Plasma for Improving Surface Hydrophilicity

Effect of Ammonia Plasma Treatment on the Properties and Cytocompatibility of A Poly(L-Lactic Acid) Film Surface

A Facile Approach to Modify Polypropylene Flakes Combining O2-plasma Treatment and Graft Polymerization of L-lactic Acid

Timeliness of Cold Plasma Treatment on Surface Modification of Polylactic Acid Fibers

Characterization of surface property of poly(lactide-co-glycolide) after oxygen plasma treatment.

Surface Modification of Poly‐l‐lactide by Photografting of Hydrophilic Polymers Towards Improving Its Hydrophilicity

Grafting of Telechelic Poly(lactic‐co‐glycolic Acid) Onto O2 Plasma‐treated Polypropylene Flakes

Ar Plasma-induced Graft Polymerization of Acrylic Acid Onto PTFE Films

Surface Modification of Poly( Lactic Acid) Film by Low-Temperature Plasma-Graft Ammonia Onto Poly(lactic Acid) Film

Improving the Cell Affinity of A Poly(D, L-Lactide) Film Modified by Grafting Collagen Via A Plasma Technique

Surface characteristics of PLA film modified by ammonia plasma

Modification of Poly(l-Lactic Acid) with L-lactic Acid / Citric Acid Oligomers

Towards a methodology for the effective surface modification of porous polymer scaffolds

Argon nonthermal plasma etching of poly(L-lactic acid) films: Tunning the local surface degradation and hydrolytic degradation rate

Enhancing the Cytocompatibility of Poly(D,L-lactide) by a Plasma Technique and Coupling Collagen

Grafting reaction of poly(D,L)lactic acid with maleic anhydride and hexanediamine to introduce more reactive groups in its bulk.

Surface modification of polylactide films and their hydrolytic degradation performances in artificial seawater