Abstract:The change in environmental temperature, especially a sharp decline of air temperature, is the critical factor for cracking damage to concrete arch dam structures. In this study, the field test and numerical calculation of the insulation effect of concrete pouring block surface were performed to prevent thermal cracks in concrete arch dams. In the field test, the temperature data of concrete at different depths measured by a distributed temperature sensing (DTS) system were analysed. The results showed that the temperature of concrete at different depths from the surface was significantly positively correlated with air temperature, and the influence depth was within 50 cm from the top surface of pouring block. During numerical simulation, the differences in surface insulation measures in insulation materials, insulation thickness, insulation time, and insulation space position were simulated and compared, considering the influence of the concrete insulation layer and cooling water. The numerical solutions showed that: (1) When the insulation material changed from 2 cm polyethylene insulation layer to 5 cm polystyrene insulation layer, the surface stress of concrete decreases from 0.86Mpa to 0.59Mpa; the insulation time was advanced to before the temperature drop, the surface stress from 0.86Mpa to 0.25Mpa; and the change of insulation position, the tensile stress of the top surface of pouring block was almost unchanged. (2) In this temperature drop, the surface insulation measure was recommended: the insulation material and thickness was the 5 cm polystyrene insulation layer, the insulation time is before the temperature drop, and the insulation position is the top surface, transverse joint surface and upstream and downstream surface of the pouring block.

Study on Concrete Surface Protection during Construction Period

Study on Temperature-Stress Simulation of RCC Dam During Construction Period

Investigation and Control of Cracks in Wet Joint of Concrete Box Girders

Finite element analysis of temperature effect and crack-control measures for ultra-long concrete structures

Study on Early Age Concrete Surface Insulation During a Cold Wave

Research on early-period concrete fracturing caused by short-duration storms

Early Age Properties and Cracking Control of Concrete

Analysis on surface protection time for concrete at early age in winter

Influence of Permanent Superficial Heat Preservation on the Temperature Stress During the Construction Period of Longhuakou RCC Gravity Dam

Control Measures for Preventing Crack on the Surface of Mass Concrete Abutment in Early Stage

Research on the Temperature Crack of Erosion- and Abrasion-resisting Concrete in Construction of the Jinghong Hydropower Project

Study on temperature control for key components of high concrete dam

Study on Thermal Stress and Temperature Cracks Control of Longlin Roller Compacted Concrete Gravity Dam

Simulative Research on Concrete Insulation of Tongzilin Hydropower Station During Construction Period when Encountering Cold Wave

Effects of controlled permeability formwork on surface properties and early age shrinkage of concrete

Research on Crack-Resisting Construction Design Method of Concrete Small Cavity Block Building Based on Temperature Effect

Field Test and Numerical Simulation of the Thermal Insulation Effect of Concrete Pouring Block Surface Based on DTS

Simulation of Thermal Stress and Control Measures for Rock-Filled Concrete Dam in High-Altitude and Cold Regions

Numerical Analysis of Softening Relationship for Early-Age Concrete

Research on Concrete Temperature Control Measures in Deep Hole Area of Super High Arch Dam

Analysis on the Cause of Cracks of High RCC Dam in Cold and Arid Area