Abstract:While the addition of WC increases the hardness and wear resistance of coatings, an excessive WC content can also induce crack initiation and propagation, increasing brittleness and leading to premature failure. Therefore, in this study, WC particles were incorporated into nickel-based coatings by plasma-arc surfacing to optimize their content and distribution, balancing their tensile properties and wear resistance. The coatings were comprehensively evaluated through microstructural analysis, hardness testing, wear resistance assessment, and tensile testing. The results show that as the mass fraction of WC increased from 45% to 65%, the increase in carbon significantly promoted the formation of M7C3, M6C, and M23C6 carbides and suppressed the formation of the γ-phase. The microstructural analysis showed that the content of massive carbides increased significantly with the increasing WC content, and the XPS analysis further confirmed that the changes in the WC and Cr7C3 phases were particularly pronounced in the high-WC coating. The 65% WC coating showed higher hardness (a 232 increase in HV1.0), a lower and more stable coefficient of friction (0.42), and better wear resistance than the 45% WC coating, with a wear rate of 3.329 × 10−6 mm3/(N·m)−1, which was 3.709 × 10−6 mm3/(N·m)−1 lower than that of the 45% WC coating. The conventional tensile test results show that the maximum stress and strain of the 45% WC coating were 71% and 36% higher than those of the 65% WC coating, respectively. In addition, the 45% WC coating exhibited better ductility and quasi-cleavage characteristics, whereas the 65% WC coating showed typical brittle cracking behavior. The results of the field tensile tests also showed that the fracture time of the 65% WC coating was 27 s shorter than that of the 45% WC coating. Overall, the 45% WC coating had a good combination of strength and toughness.

Rare Earth's Influence on Wear Resistance of Spray-melted Coatings with Mixture of Ni60B and 35Mass.%wc

Rare earth effect on the microstructure and wear resistance of Ni-based coatings

Rare earth effect on microstructure, mechanical and tribological properties of CoCrW coatings

Effect of Rare Earth on the Microstructure and Performance of Electrodeposited Ni-W Coatings

Effect of the Rare Earth Oxide CeO2 on the Microstructure and Properties of the Nano-WC-Reinforced Ni-Based Composite Coating

Tribological properties of rare earth oxide added Cr3C2–NiCr coatings

Effect of rare earth on microstructure and properties of the self-propagating spraying coating

Wear and corrosion mechanisms of Ni–WC coatings modified with different Y2O3 by laser cladding on AISI 4145H steel

Microstructure, mechanical properties and wear resistance of rare earth doped WC/steel matrix composites:Experimental and calculations

The preparation and properties of iron base self-fluxing alloy spray-welding coatings with different rare earths and chromium content

Tribological Behaviour of Rare-Earth Lubricating Oils

Rare earth elements modification of laser-clad nickel-based alloy coatings

Effects of Rare Earth on Composite Ni-Fe-P-RE Alloy Coating

Effect of rare-earth on microstrcture and performance of Fe powder covered electrode welded joint

Wear-resistance Performance of Spray-welding Coating by Plasma Weld-surfacing

Effect of Y2O3 addition on the organization and tribological properties of Ni60A/Cr3C2 composite coatings obtained by laser-cladding

Optimizing Wear Resistance and Tensile Strength of Nickel-Based Coatings through Tungsten Carbide Reinforcement

Effects of WC mass fraction on microstructure and tribological behavior of plasma sprayed FeMnCoCr–WC coatings

Effect of rare earth cerium on microstructure and wear resistance of Ni-base alloy laser-cladded coating

Effect of La2O3 addition on wear properties of Ni60a/SiC coating using laser-cladding

Study on the abrasive resistance of Ni-based coatings containing WC hard phase