Abstract:In this study, Co(1.1)Zn(0.9)TiO(4 )ceramics were sintered at 1200 degrees C using a solid sintering method. The ceramics exhibited excellent microwave dielectric properties: the quality factor (Qxf) = 55,554.1 GHz, the dielectric constant (epsilon(r)) = 16.243 and a temperature coefficient of resonant frequency (tau(f)) = -19.88 ppm/C. X-ray diffraction patterns reveal that Co(1.1)Zn(0.9)TiO(4 )ceramics have a garnet structure, and doping with H3BO3 does not yield any other second phase other than the Co(1.1)Zn(0.9)TiO(4 )phase. The analysis of the SEM images reveals a notable enhancement in grain growth with the increase in the content of added H3BO3. And by incorporating H3BO3 into the system led to the successful decrease, the sintering temperature to below 900 degrees C. The Co1.1Zn0.9TiO4 + 4 wt% H3BO3 ceramic sintered at 900 degrees C for 4 h, shows a relatively low dielectric loss, that is, the ceramic retains a relatively good value of Qxf. The detailed microwave dielectric properties of Co1.1Zn0.9TiO4 + 4 wt% H3BO3 ceramic are as follows: Qxf = 33,615.3 GHz (at 10.744 GHz), epsilon(r) = 16.578, and tau(f )= -20.00 ppm/degrees C. Additionally, when co-fired with silver (Ag), the ceramic material did not exhibit any reactivity with the Ag electrode. This characteristic could potentially be advantageous in the fabrication of low -temperature ceramics.

Microwave dielectric properties of Li2ZnTi3O8 ceramics doped with H3BO3

Microwave dielectric properties of H 3 BO 3 –CuO co-doped 0. 85BaTi 4 O 9 –0.15BaZn 2 Ti 4 O 11 ceramics

H3BO3-doping Modification Study of BaO-3TiO2 Microwave Dielectric Ceramics

The Low-Temperature Sintering and Microwave Dielectric Properties of (zn0.7mg0.3)tio3 Ceramics with H3bo3

Low-temperature Co-Firing of Co1.1Zn0.9TiO4 Microwave Dielectric Ceramics by Doping with H3BO3

Microwave dielectric properties of H 3 BO 3 -doped Ca 0.61 La 0.39 Al 0.39 Ti 0.61 O 3 ceramics

Ceramics with h 3 bo 3 addition

Low-temperature sintering and microwave dielectric properties of (zn 0.65mg0.35)tio3-catio3 ceramics with h3bo3 addition

Low‐dielectric‐loss ZnZrNb2O8 ceramics combined with H3BO3 for low‐temperature co‐fired ceramics applications

Influence of H3BO3 or SiO2 Additive on the Microwave Dielectric Properties of CTLA Ceramics

Microstructure and microwave dielectric properties of ZnO-B2O3 doped ceramics

Doping Effects In (Ba0.85ca0.15)(Hf0.1ti0.9)O-3 Lead-Free Piezoelectric Ceramics Prepared Via Powder Injection Moulding Using Simple Binder

Bond Characteristics And Microwave Dielectric Properties Of High-Q Materials In Li-Doped Zn3b2o6 Systems

Microwave Properties of Low-Fired Li2ZnTi3O8 Ceramics Doped with CuO–Bi2O3–V2O5

Microwave dielectric properties of a novel low-temperature sintering H3BO3-added Ca2V2O7 ceramics

Microwaves dielectric properties of 3Li 2O-Nb 2O 5-6TiO 2 ceramics with B 2O 3 addition

Microwave Dielectric Properties and Low-Temperature Sintering of (zn0.8mg0.2)2sio4–tio2 Ceramics with Li2O–B2O3

Study on properties of nonstoichiometric Li(2+x)ZnTi3O(8+0.5x) microwave dielectric ceramics

Microwave dielectric properties of temperature stable Li2ZnxCo1−xTi3O8 ceramics

Research on Low Temperature Sintering of ZnO-TiO_2 Ceramics Doped with Li_2CO_3-B_2O_3-V_2O_5

Microwave dielectric properties of low-temperature sintered Ca[(Li 1/3Nb 2/3) 0.95Zr 0.05]O 3-δ-0.04TiO 2 ceramics