Phase Transitions among Four BiB3O6 Polymorphs: a Detailed Investigation

Rihong Cong,Jinlong Zhu,Yingxia Wang,Tao Yang,Fuhui Liao,Changqing Jin,Jianhua Lin

DOI: https://doi.org/10.1039/b903567m

IF: 3.756

2009-01-01

CrystEngComm

Abstract:The stability and phase transformations of the four BiB3O6 polymorphs, i.e., α-, β-, γ- and δ-BiB3O6, were investigated under different temperatures and pressures. β-BiB3O6 is a metastable phase which can only be obtained by boric acid flux method in a sealed system at low temperature. The other polymorphs, α-, γ- and δ-BiB3O6, are thermodynamic stable phases. Owing to the large kinetic effect, the phase transformations of the BiB3O6 polymorphs are generally slow, thus an extensive annealing process was used in this study. The study shows that α-BiB3O6 is the high-temperature phase and its stable area is narrow (710–715 °C) in atmospheric conditions, while γ-BiB3O6 is a stable phase in the intermediate temperature range (∼680–710 °C). The results also confirm that δ-BiB3O6 is a high-pressure phase and all other polymorphs may transfer to δ-phase under high pressure. However, the δ-phase can be obtained by annealing α- or β-BiB3O6 at relatively low temperature under ambient pressure. Therefore, δ-BiB3O6 can also be regarded as the low-temperature phase in this system. Based on the experimental results, as well as the thermodynamic principles, a pressure–temperature (P–T) phase diagram for the BiB3O6 system is proposed.