Abstract:Nano-yttrium aluminum garnet (YAG) is a promising material for use in white light-emitting diodes and biological fluorescent probe. However, its existing preparation methods often suffer from low synthesis temperature and particle agglomeration. Therefore, preparing YAG nanoparticles with both high crystallinity and high dispersibility is difficult, which severely limits the applications of nano-YAG phosphor. This work presents a salt microemulsion method that can yield YAG nanoparticles of size 4–6 nm that are dispersed at a high temperature (1000 °C). Transmission electron microscope analysis shows that the precursor particles are dispersed and isolated by nano-sized potassium sulfate particles. Because the melting point of potassium sulfate is high (1067 °C), the precursors and the YAG nanoparticles are always dispersed and isolated by the solid potassium sulfate salt during calcination at high temperatures, resulting in the formation of dispersed YAG nanoparticles with good crystallinity. The reflection spectrum of nano-YAG exhibited a redshift compared to that of bulk YAG. When the Ce content is 0.06, the nano-YAG phosphor exhibited the highest internal photoluminescence quantum yield of 51.2%, and the decrease in the particle size did not increase the quenching concentration. The nano-YAG prepared at a high temperature also exhibited improved optical stability: The luminescence intensity of the nano-YAG decreased by only~ 16% after 48 h of irradiation using blue laser. The obtained 4–6-nm-sized Y3Al5O12:Ce nanophosphors are expected to be ideal materials for novel fluorescent probes and preparation of transparent ceramics.

Luminescence Properties of Garnet Lu3Al5O12:Ce Nano-Scale Phosphors

Luminescence Properties of Ce3+ Doped Garnet Ca2LaZr2Al3O12 Phosphors

Synthesis Study of Lu_3Al_5O_(12)(Ce) Nanoscaled Powder by Co-precipitation

Synthesis Study of Lu3al5o12(Ce) Nanoscaled Powder by Co-Precipitation

Synthesis, Structure and Photoluminescence Properties of Ca2LuHf2(AlO4)3:Ce3+, a Novel Garnet-Based Cyan Light-Emitting Phosphor

Luminescent properties of LuAG:Ce phosphors with different Ce contents prepared by a sol–gel combustion method

Synthesis and Characterization of Cerium-Doped Lutetium Aluminum Garnet Phosphors by Nitrate-citrate Sol-Gel Combustion Process

Preparation and Luminescence Properties of Ce3+/Dy3+-codoped Fluorosilicate Glass Ceramics

Spectroscopic Properties of Nano-Sized Cerium-Doped Lutetium Aluminum Garnet Phosphors Via Sol–gel Combustion Process

Optical and structural properties of the Fe 3+ -doped Lu 3 Al 5 O 12 :Ce 3+ garnet phosphor

Synthesis of (Y, Gd)3Al5O12:Ce Nanophosphor by Co-Precipitation Method and Its Luminescence Behavior

Cerium-Doped Lutetium Aluminum Garnet Phosphors and Optically Transparent Ceramics Prepared from Powder Precursors by a Urea Homogeneous Precipitation Method

LUMINESCENCE PROPERTIES OF NANO-SIZED Lu_2SiO_5:Ce PHOSPHORS PREPARED BY SOL-GEL METHOD

A Carbon-Free Sol–gel Method for Preparation of Lu 3 Al 5 O 12 : Ce 3+ Phosphors for Potential Applications in Laser Scintillators and LEDs

Luminescence investigation of Lu2MgAl4SiO12:Ce3+ and Ca2+ substituted Lu2MgAl4SiO12:Ce3+ phosphors

Synthesis and Luminescent Properties of Nano-Scale LuAG:RE3+ (ce, Eu) Phosphors Prepared by Co-Precipitation Method

Effects of local structure of Ce 3+ ions on luminescent properties of Y 3 Al 5 O 12 :Ce nanoparticles

Microstructure and Luminescence Characteristics of YxAl5O12∶Ce3+Phosphor

Pressure-Stimulated Synthesis and Luminescence Properties of Microcrystalline (Lu,Y)3Al5O12:Ce3+ Garnet Phosphors.

Luminescence Properties of Color Tunable New Garnet Structure (Lu1-Xmnx)3al2(al1-xsix)3o12: Ce3+ Solid Solution Phosphors

Preparation of Y 3 Al 5 O 12 :Ce Nanophosphors Using Salt Microemulsion Method and Their Luminescent Properties