LUMINESCENCE PROPERTIES OF NANO-SIZED Lu_2SiO_5:Ce PHOSPHORS PREPARED BY SOL-GEL METHOD

XIE Jianjun,LIN Ting,SHI Ying,SONG Guoxin,WU Weiping

DOI: https://doi.org/10.14062/j.issn.0454-5648.2010.10.007

2010-01-01

Abstract:Cerium-doped lutetium silicate(Lu2SiO5:Ce) powder was prepared by the sol-gel method.Based on the measurements of X-ray diffraction,transmission electron microscopy,photoluminescence,X-ray excitated emission and luminescence decay time,the phase structure and luminescence properties of the nano-scale Lu2SiO5:Ce powder were investigated.The results show that the pure crystalline Lu2SiO5:Ce with uniform size of about 40 nm is obtained after calcined at 1 000 ℃ for 2 h.The strongest excitation peak of Lu2SiO5:Ce powder locates at 360 nm in excitation spectra,and a broad emission peak with a centric wavelength of 407 nm is located at around 398-407 nm in the emission spectra excitated by 360 nm,which corresponds to the typical 4f-5d electronic transitions of Ce3+.The X-ray excitated emission spectra exhibit that the Lu2SiO5:Ce powder has short decay luminescent behaviors,and the two fitted decay time τ1 and τ2 reach 10.98 and 39.32 ns,which account for the luminescence intensity of 73.38% and 21.29%,respectively.