TiO_2/SiO_2 catalyst for photodegradation of azo dyes

Wang Kan,Chen Yingxu

2008-01-01

Abstract:The TiO2/SiO2(31% TiO2 by weight) catalyst was prepared by the acid-catalyzed sol method from the base silica gel;both were characterized by XRD,TG/DTA,SEM,and BET.The loading of TiO2 reduced the base gel’s specific surface area(from 347 m2/g to 225 m2/g),with most reduction in meso pores,and its average pore size(from 9.0 nm to 6.8 nm),while the silica base stabilized the crystalline structure of TiO2.The new catalyst was an effective adsorbent as well as a powerful catalyst.In a comparative study of adding 2 g the TiO2/SiO2 and P-25(a commercial TiO2) to each of 1 L of 80mg/L solution of AO7(an azo dye),adsorption on TiO2/SiO2 during the 1 h of contact in dark resulted in 41.5% reduction in AO7 vs.15.5% reduction by adsorption on P-25;the first order reaction rate constant of the photodegradation taking place during the next 13 h of contact under visible light was 0.278 h-1 for the TiO2/SiO2 and 0.116 h-1 for P-25.The base silica gel was not effective as a catalyst.The photodegradation was initiated by the adsorption of energized AO7 molecules on the catalyst.The TiO2/SiO2 catalyst settled readily and was easily collected for reuse.