The Effect of Multilayer Structure on Magnetic Properties of FePt Thin Films

Kaifeng Dong,Xiaofei Yang,Junbing Yan,Weiming Cheng,Xiaomin Cheng
DOI: https://doi.org/10.1016/s1006-7191(08)60066-6
2009-01-01
Abstract:The Fe/Pt multilayer films with different structures were deposited by RF magnetron sputtering on glass substrates, and the L1(0)-FePt films were obtained after the as-deposited samples were subjected to vacuum annealing at various temperatures. Results show that the Fe/Pt multilayer structure can effectively reduce the ordering temperature of FePt film, and the in-plane coercivity of [Fe (5.2 nm)/Pt (5.2 nm)](7) multilayers can reach 161.2 kA/m after annealed at 350 degrees C for 30 mm. When Fe and Pt layer thickness is equal, the coercivity of the film is the largest. On the other hand, the different Fe-Pt crystalline phases such as Fe3Pt and FePt3 phases are formed after annealing when the thickness ratio of Fe/Pt deviates from 1 after annealing. When Fe and Pt have the same thickness, the thinner single layer gets the lower ordering temperature and the larger coercivity.
What problem does this paper attempt to address?