Abstract:A novel composite membrane with a three-layer structure has been prepared. The top layer is a thin dense film of chitosan crosslinked with glutaraldehyde, and the support layer is made of microporous polyacrylonitrile (PAN). Between the dense and the microporous layer, there is an intermolecular crosslinking layer. The performance data show that this is an excellent pervaporation membrane for alcohol dehydration and one-stage separation is attainable for some alcohol/water mixtures such as ethanol/water and isopropanol/water systems, which has a good separation factor of 1410 and a good flux of 0.33 kg m(-2) h(-1) for the EtOH/H2O mixture, and 5000 and 0.43 kg m(-2) h(-1) for the i-PrOH/H2O mixture using 90 wt-% alcohol concentration at 70 degrees C,Using 90 wt % methanol aqueous solution at 60 degrees C, a flux of 0.17 kg m-2 h-l and selectivity of 123 are also obtained. The structure and performance of the novel composite membrane varies with conditions of membrane preparation, such as hydrolysis degree of PAN membrane, content of crosslinking agent, and heat-curing temperature. The results indicate that the separation factor and the permeation rate of this novel composite membrane increase with the increase of operating temperature. At the same time, the pervaporation properties can be adjusted by changing the structure of the top layer and the middle layer. (C) 2000 John Wiley & Sons, Inc.

Study of a New Pervaporation Membrane Part I. Preparation and Characteristics of the New Membrane

Sodium Alginate and Poly Vinyl Alcohol Hollow Fiber Composite Membrane for Dehydration of Isopropanol

Process Design of Continuous-Flow Pervaporation Separation for Alcohol Dehydration

Comprehensive Analysis on Anomalous Phenomenon of Ethanol-Soluble PVB Membrane for Ethanol Recovery Via Pervaporation

Preparation and characterization of polyelectrolyte complex membranes bearing alkyl side chains for the pervaporation dehydration of alcohols

A novel composite chitosan membrane for the separation of alcohol-water mixtures

Progresses in the Modification and Application of Poly(vinyl Alcohol) Membrane

Vtos Cross-Linked Pdms Membranes for Recovery of Ethanol from Aqueous Solution by Pervaporation

Studies on Alcohol Permselective Performance of a Novel Composite Membrane

Separation of Alcohol-Water Mixture by Pervaporation Through A Novel Natural Polymer Blend Membrane-Chitosan/Silk Fibroin Blend Membrane

Novel carbon nanotube/chitosan hybrid membranes for the separation of ethanol/water mixtures by pervaporation

Pervaporation properties of a three-layer structure composite membrane

Pervaporation Separation of Ethanol from Aqueous Solution by PDMS Membranes Crosslinked with VTES

Poly (vinyl Alcohol)/Cellulose Nanocomposite Pervaporation Membranes for Ethanol Dehydration

High Flux and Ultra‐thin Poly‐dimethyldiethoxysilane/poly(vinylidene Fluoride) Composite Membrane for Alcohols Recovery from Aqueous Solution by Pervaporation

Pervaporation of modified composite membrane for dehydration of micro-water isopropanol

Chitosan/poly(tetrafluoroethylene) Composite Membranes Using in Pervaporation Dehydration Processes

Pervaporation Properties and Characterization of Poly (vinyl Alcohol)/Cellulose Nanocrystal Composite Membranes

Preparation and pervaporation performance of PVA membrane with biomimetic modified silica nanoparticles as coating

Pervaporation performance of PDMS composite membranes for separation of ethanol/water mixtures(Ⅱ)and effect of membrane preparation conditions

Preferential Separation of Ethanol from Aqueous Solution Through Hydrophilic Polymer Membranes