Abstract:Bimetallic three-point-bending specimens and four-point-bending fatigue test specimens were produced from strength mismatched stainless steel/low carbon steel bi-material. Both the J resistance curves and fatigue crack growth behavior were investigated for the bi- and bulk materials. The results showed that a crack initiated easily at the interface, and crack growth resistance along interface was inferior to that of the corresponding bulk materials under either static or dynamic loading conditions.

Crack Propagation Resistance along Strength Mismatched Bimetallic Interface