Abstract:Mesoporous carbon materials with ultra-thin carbon pore walls and highly dispersed Ni nanoparticles have been successfully prepared by using two different SBA-15 silicas as hard templates and 2,3-dihydroxynaphthalene (DHN) as a carbon precursor. The nickel precursor was a concentrated nickel nitrate hexahydrate [Ni(NO3)(2)center dot 6H(2)O] solution in 2-propanol, which was added to the carbon-silica nanocomposite prior to thermal treatment. The samples studied were analyzed by thermogravimetry (TG), nitrogen adsorption at -196 degrees C, powder X-ray diffraction (XRD), Raman spectroscopy, scanning and transmission electron microscopy (STEM), and in situ electron diffraction X-ray spectroscopy (EDX). While TG analysis revealed carbon contents lower than 30 wt.-%, nitrogen adsorption provided information about the homogeneity of the carbon thin film deposited onto the mesopore walls of the ordered silica templates SBA-15. The templates, carbon-silica nanocomposites, and carbon inverse replicas with nickel nanoparticles exhibit uniform pores, high surface areas, and large pore volumes. Partially graphitic carbon was identified by the presence of a characteristic G band in the Raman spectra, whereas the diffraction peak attributed to the stacking of graphene planes was not observed by powder XRD. The presence of ordered domains in the carbon materials studied was confirmed by small angle XRD and STEM imaging. In addition, the STEM images revealed that the nickel nanoparticles are uniform in size, ca. 3 nm, and are homogeneously dispersed on the tubular carbon walls. A few larger clusters of nickel, ca. 60 nm, present on the external surface, were identified by powder XRD as metallic Ni. The in situ EDX revealed that the small nanoparticles are largely composed of Ni with traces of NiO. Similar nanoparticle dispersions have been reported only for Ni-containing multiwalled carbon nanotubes (CNTs), whereas previously reported ordered mesoporous carbon materials, CMK-3, possess larger Ni/NiO nanoparticles. ((C) Wiley-VCH Verlag GmbH & Co. KGaA, 69451 Weinheim, Germany, 2009)

Planting of Bis(1,5-Cyclooctadiene) Nickel Upon Silica to Harvest NiO (<5 Nm) Nanoparticles in a Silica Matrix

PREPARATION OF NiO NANOPARTICLES ON THE SILICA SURFACE BY ADSORPTION PHASE SYNTHESIS AND ITS REGULATION ON MORPHOLOGY OF NiO PARTICLES

Mesoporous Carbon Materials with Ultra‐Thin Pore Walls and Highly Dispersed Nickel Nanoparticles

Interface-controlled synthesis of nickel phyllosilicate for efficient CO 2 hydrogenation to methane: Breaking limitation of the conventional silica-surface-controlled synthesis

Phase-controlled Synthesis of Nickel Silicide Nanostructures

Dispersion of Nano Nickel Particles over SBA-15 Modified by Carbon Films on Pore Walls

Formation Combined with Intercalation of Ni and Its Alloy Nanoparticles within Mesoporous Silica for Robust Catalytic Reactions

Ni/SiO2 catalyst with hierarchical pore structure prepared by phase separation in sol–gel process

Porous Hierarchical Nickel Nanostructures and Their Application As a Magnetically Separable Catalyst

Surface Silicide Facilitates the Co2 Reduction Performance of Ni Oxide Supported Pd Nano-Islands

Synthesis of nickel oxide nanoparticles by Sol-gel method

Preparation and characteristics of NiO-coated nano-fibriform silica

Highly Dispersed Nickel Particles Encapsulated in Multi‐hollow Silicalite‐1 Single Crystal Nanoboxes: Effects of Siliceous Deposits and Phosphorous Species on the Catalytic Performances

Rapid construction of nickel phyllosilicate with ultrathin layers and high performance for CO2 methanation

Template-free Sonochemical Synthesis of Hierarchically Porous NiO Microsphere.

Design of Nickel-Containing Nanocomposites Based on Ordered Mesoporous Silica: Synthesis, Structure, and Methylene Blue Adsorption

Synthesis of hierarchical tree-like and jellyfish-like silicon oxide nanostructures.

Low temperature in situ immobilization of nanoscale fcc and hcp polymorphic nickel particles in polymer-derived Si-C-O-N(H) to promote electrocatalytic water oxidation in alkaline media

Evolution of Nickel Speciation During Preparation of Ni-SiO(2) Catalysts: Effect of the Number of Chelating Ligands in [Ni(en)x(h2o)6-2X]2+ Precursor Complexes.

Facile synthesis of nickel nanoparticles supported on carbon and silica matrix via a novel silica sol–gel process

Ensemble Effect of the Nickel-Silica Interface Promotes the Water-Gas Shift Reaction